Moisture-permeable waterproof fabric and process for producing same
A moisture-permeable waterproof fabric which has a well-balanced combination of moisture permeability and waterproofing properties and has excellent strength, in particular, tensile strength, is provided without increasing environmental burden. A synthetic-polymer solution comprising a synthetic polymer consisting mainly of a polyurethane, fine inorganic particles, and a polar organic solvent is applied to one surface of a fibrous fabric and then brought into contact with a gaseous phase in which waterdrops having an average particle diameter of 1-30 μm have been evenly dispersed, thereby making the synthetic polymer semisolid. The fabric is then immersed in water to completely solidify the polymer and thereby obtain a moisture-permeable waterproof fabric comprising the fibrous fabric and, united to one surface thereof, a microporous film of a single-layer structure comprising the synthetic polymer consisting mainly of a polyurethane (the number of micropores having a pore diameter of 0.1-5 μm is (5-200)×10 4 /mm 2 in a vertical cross-section, and the film has a tensile strength of 3-80 MPa, a moisture permeability as measured by the calcium chloride method of 6,000 g/m 2 ·24 hr or higher or a moisture permeability as measured by the potassium acetate method of 6,000 g/m 2 ·24 hr or higher, and a water pressure resistance of 60 kPa or higher).
1. A process for producing a moisture-permeable waterproof fabric which comprises applying a synthetic polymer solution comprising a synthetic polymer consisting mainly of a polyurethane resin, 5-75% by weight of fine inorganic particles based on the total solid content and a polar organic solvent to one surface of a fibrous fabric, bringing said synthetic polymer solution into contact with a gas phase to make the synthetic polymer into a state of semi-coagulation, wherein the gas phase contains water fog having uniformly dispersed water particles that have an average particle diameter of 1-30 μm, and subsequently, immersing in water said fibrous fabric having thereon said synthetic polymer solution to completely coagulate the synthetic polymer.
2. The process for producing a moisture-permeable waterproof fabric according to claim 1 , wherein said step of bringing into contact with said gas phase is carried out by exposing said synthetic polymer solution to a gas phase, wherein the gas phase contains water fog having uniformly dispersed water particles that have an average particle diameter of 1-30 μm.
3. The process for producing a moisture-permeable waterproof fabric according to claim 1 , wherein said step of bringing into contact with said gas phase is carried out by spraying a gas phase onto said synthetic polymer solution, wherein the gas phase contains water fog having uniformly dispersed water particles that have an average particle diameter of 1-30 μm.
4. A process for producing a moisture-permeable waterproof fabric which comprises applying a synthetic polymer solution comprising a synthetic polymer consisting mainly of a polyurethane resin, 5-75% by weight of fine inorganic particles based on the total solid content and a polar organic solvent to a releasable base material,
bringing said synthetic polymer solution into contact with a gas phase to make the synthetic polymer into a state of semi-coagulation, wherein the gas phase contains water fog having uniformly dispersed water particles that have an average particle diameter of 1-30 μm, immersing in water said releasable base material having thereon said synthetic polymer solution to completely coagulate the synthetic polymer to form a microporous layer film, and subsequently, laminating said microporous layer film to one surface of a fibrous fabric via an adhesive to produce a moisture-permeable waterproof fabric.
5. The process for producing a moisture-permeable waterproof fabric according to claim 4 , wherein said step of bringing into contact with said gas phase is carried out by exposing said synthetic polymer solution to a gas phase, wherein the gas phase contains water fog having uniformly dispersed water particles that have an average particle diameter of 1-30 μm.
6. The process for producing a moisture-permeable waterproof fabric according to claim 4 , wherein said step of bringing into contact with said gas phase is carried out by spraying a gas phase onto said synthetic polymer solution, wherein the gas phase contains water fog having uniformly dispersed water particles that have an average particle diameter of 1-30 μm.