Adhesion-promoting additive for an ink for imprinting glass
The invention relates to an adhesion-promoting additive for an ink for imprinting glass comprising at least one silane, and at least one reticulating agent based on an organic ester of o-silica.
1. An ink, comprising:
a solvent;
a binding agent;
a pigment; and
an additive, wherein the additive comprises:
a silane with a methacrylic acid group;
at least one reticulating agent based on an organic ester of o-silica,
a silane with an epoxide group; and
a silane with an amino group, wherein the ratio by weight of said silanes with epoxide or amino or the methacrylic acid group is in the range of 1:0.1:50 to 1:1:1.
2. The ink according to claim 1 , wherein the proportion of additive is selected from a range with a lower limit of 5 wt. % and an upper limit of 70 wt. %.
3. The ink according to claim 1 , further comprising at least one viscosity regulator, wherein the ratio of the total amount of viscosity regulator to the amount of additive is selected from a range with a lower limit of 0.5:1 and an upper limit of 10:1.
4. The ink according to claim 1 , wherein the ester of o-silica is selected from a group of compounds with the general formula SiO 4 R u R v R w R x , wherein R v , R w , R x are formed respectively by H or a C 1 -C 8 group and R u is a C 1 -C 8 group.
5. The ink according to claim 1 , wherein the proportion of the ester of o-silica is selected from a range with a lower limit of 1 wt. % and an upper limit of 90 wt. %.
6. The ink according to claim 1 , wherein the reticulating agent comprises an organic polymer or its monomer prestage.
7. The ink according to claim 6 , wherein the organic polymer is selected from the group consisting of acrylate resins, silicon resins, polyurethane resins, polyamide resins, and polyimide resins.
8. The ink according to claim 6 , wherein the proportion of organic polymer is selected from a range with a lower limit of 0.5 wt. % and an upper limit of 50 wt. %.
9. The ink according to claim 1 , wherein the functional group is arranged terminally on the silane.
10. The ink according to claim 1 , wherein the silane with the epoxy group is 3-glycidyloxypropyltrimethoxy silane, the silane with the amino group is 3-aminopropyltriethoxy silane, and the silane with the methacrylic acid group is 3-methacryloxypropyltrimethoxy silane.
11. The ink according to claim 1 , wherein the proportion of the silanes is selected from a range with a lower limit of 1 wt. % and an upper limit of 80 wt. %.
12. The ink according to claim 1 , further comprising at least one UV initiator and/or a thermal initiator.
13. The ink according to claim 12 , wherein the proportion of the at least one initiator is selected from a range with a lower limit of 0.5 wt. % and an upper limit of 25 wt. %.
14. The ink according to claim 1 , further comprising at least one surfactant.
15. The ink according to claim 14 , wherein the proportion of surfactant is selected from a range with a lower limit of 0.5 wt. % and an upper limit of 50 wt. %.