Polytetrafluoroethylene resins that can be processed by shaping, shaped products thereof, and processes for producing the resins and shaped products
A polytetrafluoroethylene resin comprising polytetrafluoroethylene having a two-dimensional branched structure in the molecule is produced by exposing polytetrafluoroethylene to an ionizing radiation at a dose of no more than 10 kGy.
1. A process for producing a polytetrafluoroethylene resin having a two-dimensional branch structure, comprising polytetrafluoroethylene having a two-dimensional branched structure in the molecule, which process comprises
exposing polytetrafluoroethylene to an ionizing radiation at a dose of less than 1 kGy at a temperature not lower than a melting point of un-irradiated polytetrafluoroethylene and in the absence of oxygen and further comprises any one of the following steps:
extruding the irradiated polytetrafluoroethylene;
compressing the irradiated polytetrafluoroethylene in a mold;
rolling the irradiated polytetrafluoroethylene; or
melt spinning the irradiated polytetrafluoroethylene.
2. A process for producing the polytetrafluoroethylene resin according to claim 1 , wherein the polytetrafluoroethylene to be exposed to the ionizing radiation is polytetrafluoroethylene which has been heated to a molten state and then cooled.
3. A process for producing the polytetrafluoroethylene resin according to claim 1 , the process comprising extruding the irradiated polytetrafluoroethylene at a temperature not lower than a melting point of the irradiated polytetrafluoroethylene to form a rod, fiber, tube or a film of the irradiated polytetrafluoroethylene.
4. A process for producing the polytetrafluoroethylene resin according to claim 1 , the process comprising compressing the irradiated polytetrafluoroethylene in a mold at a temperature not lower than a melting point of the irradiated polytetrafluoroethylene to form a shaped article of the irradiated polytetrafluoroethylene.
5. A process for producing the polytetrafluoroethylene resin according to claim 1 , the process comprising rolling the irradiated polytetrafluoroethylene at a temperature below a melting point of the irradiated, polytetrafluoroethylene to form a shaped article of the irradiated polytetrafluoroethylene.
6. A process for producing the polytetrafluoroethylene resin according to claim 1 , the process comprising melt spinning the irradiated polytetrafluoroethylene to form a monofilament of the irradiated polytetrafluoroethylene.
7. A process for producing the polytetrafluoroethylene resin according to claim 1 , the process comprising melt extruding the irradiated polytetrafluoroethylene to form a lamination of the irradiated polytetrafluoroethylene.
8. A process for producing polytetrafluoroethylene having a branched structure, the process comprising:
heating polytetrafluoroethylene at a temperature not lower than the melting point thereof;
irradiating the heated polytetrafluoroethylene with an ionizing radiation at a dose of less than 1 kGy in the absence of oxygen and further comprises any one of the following steps:
extruding the irradiated polytetrafluoroethylene;
compressing the irradiated polytetrafluoroethylene in a mold;
rolling the irradiated polytetrafluoroethylene; or
melt spinning the irradiated polytetrafluoroethylene.