Resin composition, molded article, multilayered pipe and method for producing the same
An object of the present invention is to provide a multilayered pipe having a layer comprising a resin composition containing EVOH, which is unlikely to exhibit the occurrence of cracking in the EVOH layer due to oxidative degeneration and has excellent gas barrier property even during long-term usage at high temperatures, and also to provide a resin composition for obtaining the multilayered pipe. The present invention relates to a resin composition containing 0.001 to 5 parts by mass of an antioxidant (B) and 0.00001 to 0.3 parts by mass of a conjugated polyene compound (C) having a molecular weight of 1000 or less, relative to 100 parts by mass of an ethylene-vinyl alcohol copolymer (A).
1. A hot water circulation pipe, comprising a multilayered pipe, said multilayered pipe comprising a layer comprising a resin composition, wherein said resin composition comprises an ethylene-vinyl alcohol copolymer (A) and, relative to 100 parts by mass of the ethylene-vinyl alcohol copolymer (A), 0.001 to 5 parts by mass of an antioxidant (B), and 0.00001 to 0.3 parts by mass of a conjugated polyene compound (C) having a molecular weight of 1000 or less.
2. The hot water circulation pipe according to claim 1 , wherein said resin composition comprises 0.00005 to 0.2 parts by mass of the conjugated polyene compound (C).
3. The hot water circulation pipe according to claim 2 , wherein said resin composition comprises 0.0001 to 0.15 parts by mass of the conjugated polyene compound (C).
4. The hot water circulation pipe according to claim 1 , wherein the conjugated polyene compound (C) is at least one selected from a group consisting of sorbic acid, sorbic acid salt, and myrcene.
5. The hot water circulation pipe according to claim 4 , wherein the conjugated polyene compound (C) is sorbic acid, a salt thereof, or both.
6. The hot water circulation pipe according to claim 1 , wherein said resin composition comprises 0.01 to 4 parts by mass of the antioxidant (B).
7. The hot water circulation pipe according to claim 1 , wherein the antioxidant (B) is a compound comprising a hindered amine group, a compound comprising a hindered phenol group, or both.
8. The hot water circulation pipe according to claim 1 , wherein the layer comprising the resin composition is an outermost layer of the multilayered pipe.
9. A method for producing the hot water circulation pipe according to claim 1 , the method comprising molding an object from the resin composition followed by cooling with water having a temperature of 10 to 70° C. immediately after the molding.
10. The hot water circulation pipe according to claim 1 , wherein:
the conjugated polyene compound (C) is at least one selected from the group consisting of sorbic acid, sorbic acid salt, and myrcene, and
the antioxidant (B) is a compound comprising a hindered amine group, a compound comprising a hindered phenol group, or both.
11. The hot water circulation pipe according to claim 10 , wherein said resin composition comprises 0.0001 to 0.15 parts by mass of the conjugated polyene compound (C) and 0.01 to 4 parts by mass of the antioxidant (B).
12. The hot water circulation pipe according to claim 1 , wherein the conjugated polyene compound (C) has a molecular weight of 500 or less.
13. The hot water circulation pipe according to claim 1 , wherein the conjugated polyene compound (C) has seven or fewer carbon-carbon double bonds to conjugate.
14. The hot water circulation pipe according to claim 12 , wherein the conjugated polyene compound (C) has seven or fewer carbon-carbon double bonds to conjugate.
15. A floor heating system based on hot water circulation, comprising the hot water circulation pipe of claim 1 .