Multilayer porous membrane and production method thereof
The present invention provides a multilayer porous membrane having both high safety and practicality, especially as a separator for a non-aqueous electrolyte battery and comprising a porous layer containing an inorganic filler and a resin binder on at least one surface of a polyolefin resin porous membrane, wherein the porous layer simultaneously satisfies the following (A) to (C): (A) the inorganic filler has an average particle diameter of 0.1 μm or more and 3.0 μm or less, (B) a ratio of an amount of the resin binder to a total amount of the inorganic filler and the resin binder is 1% or more and 8% or less in terms of volume fraction, and (C) a ratio of a layer thickness of the porous layer to a total layer thickness is 15% or more and 50% or less.
1. A separator for a non-aqueous electrolyte battery comprising a multilayer porous membrane comprising a porous layer containing an inorganic filler and a resin binder adhered to at least one surface of a polyolefin resin porous membrane, wherein the porous layer simultaneously satisfies the following (A) to (C):
(A) the inorganic filler has an average particle diameter of 0.1 μm or more and 3.0 μm urn or less,
(B) a ratio of an amount of the resin binder to a total amount of the inorganic filler and the resin binder is 0.5% or more and 8% or less in terms of volume fraction,
(C) a ratio of a layer thickness of the porous layer to a total layer thickness of the porous layer and the polyolefin resin porous membrane is 15% or more and 50% or less, and wherein a maximum MD value of a load generated as the polyolefin resin porous membrane was heated from temperature of 30° C. to 200° C. is 7 g or less.
2. The separator according to claim 1 , wherein the resin binder is a polyvinyl alcohol having a degree of saponification of 85% or more.
3. The separator according to claim 1 , wherein the polyolefin resin porous membrane surface facing the porous layer has a wetting index of 40 mN/m or more.
4. A non-aqueous electrolyte battery using a separator according to claim 1 .
5. A method of producing the separator according to claim 1 , comprising applying a dispersion solution containing the inorganic filler and the resin binder on at least one surface of the polyolefin resin porous membrane.