Production of an article by selective fusion of polymer powder layers

1. A method of manufacturing an article, the method comprising manufacturing the article by selective fusion of layers using a powder comprising at least one copolyamide having an enthalpy of cold crystallization of less than 80 J/g, as measured by protocol P;

wherein the at least one copolyamide comprises at least 80 mol % of caprolactam monomer or the corresponding amino acid, based on the number of moles of the total mixture of monomers and comonomers, and at least one aromatic or cycloaliphatic comonomer; and

wherein the protocol P involves measuring the enthalpy of cold crystallization by modulated differential calorimetry analysis that comprises:

a) first holding the copolyamide at a temperature of 25° C. for 5 minutes,

b) performing a modulated rise in temperature to 250° C. at a rate of 3° C./min with a sinusoidal amplitude of 0.48° C. and a period of 1 minute, and recording a signal, and

c) measuring an area of exothermic peak ΔH cc , corresponding to the enthalpy of cold crystallization of the copolyamide.

2. The method as defined by claim 1 , wherein the aromatic or cycloaliphatic comonomer of the copolyamide has at least one function selected from the group consisting of:

an amine function Am, that can form an amide bond with a carboxylic acid function of the constituent monomer of the polyamide;

a carboxylic acid function Ac, that can form an amide bond with an amine function of the constituent monomer of the polyamide;

an alcohol function OH, that can form an ester bond with a carboxylic acid function of the constituent monomer of the polyamide; and

a dicarboxylic acid function DA, that can form an imide bond with an amine function of the constituent monomer of the polyamide.

3. The method as defined by claim 2 , wherein the comonomer is represented by the formula (I) below:

R(Am) w -(Ac) x (OH) y (DA) z   (I)

in which:

R is a linear, branched, aliphatic, aromatic, or cycloaliphatic hydrocarbon radical;

w is between 0 and 4;

x is between 0 and 4;

y is between 0 and 4;

z is between 0 and 4; and

w+x+y+z is greater than or equal to 1.

4. The method as defined by claim 1 , wherein the comonomer is selected from the group consisting of:

amino acids or aminocarboxylic acids, or lactams;

diamines;

diacids;

monoacid or monoamine compounds;

hydroxy acids;

lactones;

diols; and

monomers comprising two carboxylic acid functions, allowing formation of aliphatic, aromatic, or cycloaliphatic imide functions.

5. The method as defined by claim 1 , wherein the aromatic comonomer is selected from the group consisting of: terephthalic acid, isophthalic acid, benzoic acid, phenylenediamine, 1-naphthoic acid, anthracene-9-carboxylic acid, aniline, naphthylamine, 1,8-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, 5-hydroxyisophthalic acid, 5-sulfoisophthalic acid, 2,3-diaminonaphthalene, 1,5-diaminonaphthalene, 4-aminobenzoic acid, 4-hydroxybenzoic acid, 1-hydroxy-2-naphthoic acid, 3-hydroxy-2-naphthoic acid, 4,4′-diaminodiphenylmethane acid, 4-aminophenyl ether, trimesic acids, trimellitic acid, pyromellitic acid, 3,4,9,10-perylenetetracarboxylic acid, 5-aminoisophthalic acid, 3,5-diaminobenzoic acid, hydroquinone, resorcinol, bisphenol A, 4,4′-oxydiphenol, and tetrahydrophthalic anhydride.

6. The method as defined by claim 1 , wherein the cycloaliphatic comonomer is selected from the group consisting of: isophoronediamine, bis(3,5-dialkyl-4-aminocyclohexyl)methane, bis(3,5-dialkyl-4-aminocyclohexyl)ethane, bis(3,5-dialkyl-4-aminocyclohexyl) propane, bis(3,5-dialkyl-4-aminocyclohexyl) butane, bis(3-methyl-4-aminocyclohexyl)methane, p-bis(aminocyclohexyl)methane, and isopropylidenedi(cyclohexylamine), 1,4-dicarboxycyclohexane, 4,4′-diamino-3,3′-dimethyldicyclohexylmethane, 1,4-diaminocyclohexane, hexahydroterephthalic acid, 4-amino-2,2,6,6-tetramethylpiperidine (TAD), piperazine, N-(2-aminoethyl)piperazine, N,N′-bis(2-aminoethyl)piperazine, 1,2-diaminocyclohexane, N,N′-bis(2-aminoethyl)imidazolidone, N-(2-hydroxyethyl)piperazine, isosorbide, isomannide, 1,4-cyclohexanediol, N,N′-bis(2-hydroxyethyl)imidazolidone, 4-amino-1-cyclohexanecarboxylic acid, and trans-1,2-diaminocyclohexane-N,N,N′,N′-tetraacetic acid.

7. The method as defined by claim 1 , wherein the powder is produced by:

a) melt-mixing the copolyamide with a compound A consisting of a polymeric material comprising at least one part of its structure that is compatible with said copolyamide and at least one part of its structure that is not compatible and is insoluble in said copolyamide, to give a dispersion of discrete particles of copolyamide;

b) cooling this mixture to a temperature lower than the softening temperature of the copolyamide; and

c) treating this cooled mixture to bring about the disintegration of the copolyamide particles.

8. The method as defined by claim 1 , wherein the powder has one or more of the following features:

a d50 particle size distribution of between 20 μm and 100 μm and also fulfilling the following relation: (d90−d10)/d50 of between 0.85-1.3;

a sphericity factor of between 0.8 and 1; and

an intraparticular porosity of less than 0.05 ml/g, especially for pore sizes of greater than or equal to 0.01 μm.

9. An article manufactured by the method as defined by claim 1 .

10. The method as defined by claim 4 , wherein the diamines are aliphatic, aromatic, or cycloaliphatic.

11. The method as defined by claim 4 , wherein the diacids are aliphatic, aromatic, or cycloaliphatic.

12. The method as defined by claim 4 , wherein the diols are aliphatic or cycloaliphatic.

13. The method as defined by claim 8 , wherein the d50 particle size distribution is between 30 and 70 μm.

14. The method as defined by claim 8 , wherein the relation (d90−d10)/d50 is 0.9-1.2.

15. The method as defined by claim 8 , wherein the sphericity factor is between 0.85 and 1.

16. The method as defined by claim 8 , wherein the intraparticular porosity is less than 0.02 ml/g.