Surface passivation of active material particles for use in electrochemical cells
Provided are methods of passivating active materials for use in electrochemical cells as well as active materials and cell components prepared using such methods. Active material particles may be combined with passivating material particles, and this combination may be mixed together using high shear mixing. The mixed combination may not include any solvents or binders. As such, drying mixing may be performed on this combination of the active material particles and passivating material particles. A passivating layer is formed on the active material particles during mixing. This passivating layer later prevents direct contact between the active material particles and the electrolyte while still allowing ionic exchange. Furthermore, the passivating layer may increase electronic conductivity between active material particles in an electrode. The passivating layer may be mechanically bonded to the surface of the active material particles rather than chemically bonded.
1. A method of passivating active materials for use in electrochemical cells, the method comprising:
combining active material particles and passivating material particles,
wherein the active material particles comprise one or more materials selected from the group consisting of lithium titanate (Li 4 Ti 5 O 12 ), lithium cobalt oxide (LiCoO 2 ), lithium nickel cobalt aluminum oxide (LiNi 0.85 Co 0.1 Al 0.05 O 2 ), lithium nickel cobalt manganese oxide (LiNi 1/3 Co 1/3 Mn 1/3 O 2 ), lithium manganese oxide (LiMn 2 O 4 ), lithium iron phosphate (LiFePO 4 ), lithium manganese iron phosphate, lithium cobalt phosphate, spinel lithium nickel manganese oxide, layered lithium nickel manganese oxide, lithium- and manganese-rich transition metal layered-oxides (LMR-NMC), and lithium iron silicate (Li 2 FeSiO 4 ),
mixing a combination of the active material particles and the passivating material particles using high shear mixing,
wherein during mixing the combination of the active material particles and the passivating material particles has a solid content of at least about 99%,
wherein mixing forms a passivating layer on the active material particles, the passivating layer comprising a material of the passivating material particles,
wherein a total surface ratio of the passivating material particles relative to the active material particles is between 1 and 5.
2. The method of claim 1 , wherein the passivating material particles comprise one or more materials selected from the group consisting of a carbon-containing material, a ceramic, and a polymer.
3. The method of claim 1 , wherein the passivating material particles comprise one or more carbon-containing materials selected from the group consisting of carbon black, activated carbon, hard carbon, soft carbon, meso carbon micro beads (MCMB), graphite, graphene, and carbon nanotubes (CNT).
4. The method of claim 1 , wherein the passivating material particles comprise graphene nano-plates.
5. The method of claim 1 , wherein the passivating material particles comprise one or more carbon-containing materials having one or more morphology structures selected from the group consisting of a needle-like structure, a plate-like structure, a spherical structure, and an irregular structure.
6. The method of claim 1 , wherein the passivating material particles comprise one or more ceramics selected from the group consisting of aluminum oxide (Al 2 O 3 ), silicon oxide (SiO 2 ), titanium oxide (TiO 2 ), and molybdenum oxide (MoO 3 ).
7. The method of claim 1 , wherein the passivating material particles comprise one or more polymers having a main chain length of at least about 50,000.
8. The method of claim 1 , wherein the passivating material particles comprise one or more polymers selected from the group consisting of polypropylene (PP), polyethylene (PE), polyvinyl chloride (PVC), polyvinyl acetate (PVA), poly acrylic acid (PAA), and poly acrylonitrile (PAN).
9. The method of claim 1 , wherein the passivating material particles have a two-dimensional shape.
10. The method of claim 1 , wherein the active material particles comprise lithium titanate (Li 4 Ti 5 O 12 ).
11. The method of claim 1 , wherein a combined average surface area of the active material particles and the passivating material particles is reduced during mixing.
12. The method of claim 1 , wherein a combined average surface area of the active material particles and the passivating material particles is reduced by at least about 5 times during mixing.
13. The method of claim 1 , wherein a weight ratio of the passivating material particles relative to the active material particles in the combination is between about 0.01 and 0.1.
14. The method of claim 1 , wherein the high shear mixing is performed using a set of three blades including a top blade, a bottom blade, and a middle blade,
wherein the top blade directs the active material particles and the passivating material particles toward the bottom blade during the high shear mixing,
wherein the bottom blade directs the active material particles and the passivating material particles toward the top blade during the high shear mixing; and
wherein the middle blade exerts a shear force on the active material particles and the passivating material particles during the high shear mixing,
the middle blade disposed between the top blade and the bottom blade.
15. The method of claim 1 , wherein the high shear mixing comprises one or more techniques selected from the group of dry-blending, ball milling, jet milling, three roller milling, grinding, attrition milling, and cryo-milling.
16. The method of claim 1 , further comprising, after mixing the combination of the active material particles and the passivating material particles using high shear mixing, adding a polymer binder to the combination, thereby forming a slurry.
17. The method of claim 16 , further comprising coating the slurry on a current collector substrate.
18. The method of claim 16 , further comprising adding a carbon-containing material to the slurry.
19. A passivated active material comprising:
active material particles comprising lithium titanate (Li 4 Ti 5 O 12 ); and
a passivating layer disposed on a surface of the active material particles,
wherein the passivating layer comprises a carbon-containing material; and
wherein a weight ratio of the passivating layer to the active material particles is between about 0.01 and 0.1; and
wherein a total surface ratio of the passivating layer relative to the active material particles is between 1 and 5.
20. A method of passivating active materials for use in electrochemical cells, the method comprising:
combining active material particles and passivating material particles,
wherein the active material particles comprise one or more materials selected from the group consisting of lithium titanate (Li 4 Ti 5 O 12 ), lithium cobalt oxide (LiCoO 2 ), lithium nickel cobalt aluminum oxide (LiNi 0.85 Co 0.1 Al 0.05 O 2 ), lithium nickel cobalt manganese oxide (LiNi 1/3 Co 1/3 Mn 1/3 O 2 ), lithium manganese oxide (LiMn 2 O 4 ), lithium iron phosphate (LiFePO 4 ), lithium manganese iron phosphate, lithium cobalt phosphate, spinel lithium nickel manganese oxide, layered lithium nickel manganese oxide, lithium- and manganese-rich transition metal layered-oxides (LMR-NMC), and lithium iron silicate (Li 2 FeSiO 4 ),
mixing a combination of the active material particles and the passivating material particles using high shear mixing,
wherein during mixing the combination of the active material particles and the passivating material particles has a solid content of at least about 99%,
wherein mixing forms a passivating layer on the active material particles, the passivating layer comprising a material of the passivating material particles,
wherein the high shear mixing is performed using a set of three blades including a top blade, a bottom blade, and a middle blade,
wherein the top blade directs the active material particles and the passivating material particles toward the bottom blade during the high shear mixing,
wherein the bottom blade directs the active material particles and the passivating material particles toward the top blade during the high shear mixing, and
wherein the middle blade exerts a force on the active material particles and the passivating material particles during the high shear mixing,
wherein the middle blade is disposed between the top blade and the bottom blade.