Method for producing release liner
Efficiently produced is a release liner including a plant-derived film as a substrate and having a good appearance, releasability, and adhesion. A method according to the present invention produces a release liner having a plant-derived film substrate and, on at least one side thereof, a release coat layer derived from a thermosetting silicone resin. The method includes the steps as follows: Step A of applying a thermosetting silicone release agent to at least one side of a plant-derived film substrate, the release agent containing 100 parts by weight of a thermosetting silicone resin and 0.05 to 0.55 part by weight of a curing catalyst; Step B of drying at 40° C. to 90° C. for 10 to 60 seconds after Step A; Step C of applying an ultraviolet ray at 50 to 300 mJ/cm 2 after Step B; and Step D of aging at 30° C. to 70° C. for 12 to 240 hours after Step C.
1. A method for producing a release liner, the release liner comprising a plant-derived film substrate; and a release coat layer lying on or over at least one side of the film substrate, the release coat layer derived from a thermosetting silicone resin, the method comprising the steps as follows:
Step A of applying a thermosetting silicone release agent to at least one side of a plant-derived film substrate, which comprised at least one selected from the group consisting of a poly(lactic acid) film, a cellulose film, and a polyamide film, to for a coat layer thereon, the thermosetting silicone release agent comprising 100 parts by weight of a thermosetting silicone resin and 0.05 to 0.55 part by weight of a curing catalyst, which comprises a platinum catalyst;
Step B of drying the coat layer after Step A at a temperature of from 40° C. to 90° C. for a duration of from 10 to 60 seconds;
Step C of applying an ultraviolet ray to the coat layer after Step B at a dose of from 50 to 300 mJ/cm 2 ; and
Step D of aging the coat layer after Step C at a temperature of from 30° C. to 70° C. for a duration of 12 to 240 hours.
2. The method for producing a release liner, according to claim 1 , wherein the poly(lactic acid) film is a biaxially stretched poly(lactic acid) film.
3. A release liner comprising a plant-derived film substrate; and a release coat layer lying on or over at least one side of the film substrate, the release coat layer derived from a thermosetting silicone resin, wherein the release liner is produced by the production method of claim 2 .
4. A release liner comprising a plant-derived film substrate; and a release coat layer lying on or over at least one side of the film substrate, the release coat layer derived from a thermosetting silicone resin, wherein the release liner is produced by the production method of claim 1 .