Welding compositions for improved mechanical properties in the welding of cast iron
A weld deposit produced from a coated welding electrode for use in welding cast irons is provided by the present invention. Preferably, in one form of the present invention, the weld deposit composition comprises between approximately 54% and approximately 60% Nickel, between approximately 3.5% and approximately 5.5% Manganese, and between approximately 0.9% and approximately 1.4% Carbon. The weld deposit is preferably formed by using a coated welding electrode having a coating composition between approximately 0.3% and approximately 4.0% Magnesium and rare earth metals and oxides. The resulting weld deposit exhibits improved ductility, fracture toughness, and resistance to cracking.
1. A welding electrode for use in welding cast irons, the welding electrode comprising:
a core wire comprising approximately 50% Nickel and approximately 50% Iron; and
a coating on the core wire comprising between approximately 0.3% and approximately 4.0% Magnesium and rare earth metals and oxides, the welding wire producing an austenitic weld deposit composition comprising:
between approximately 54% and approximately 60% Nickel;
between approximately 3.5% and approximately 5.5% Manganese; and
between approximately 0.9% and approximately 1.4% Carbon;
approximately 0.5% Silicon;
less than approximately 0.03% Sulfur;
less than approximately 0.2% Copper; less than approximately 0.5% Aluminum; and
between approximately 33.0% and approximately 41.5% Iron;
wherein the weld deposit is carbide-free and the Carbon is present in the form of nodular graphite and
wherein the weld deposit is carbide-free in a fusion zone and a mixed zone and throughout the weld structure.
2. A cast iron welded structure comprising at least one weld produced from the welding electrode of claim 1 .
3. A method of welding cast iron, the method comprising the step of using the welding electrode of claim 1 to produce the weld deposit composition.
4. The method according to claim 3 , wherein the welding comprises a process selected from a group consisting of GMAW, SMAW, SAW, and FCAW.
5. A welding electrode comprising a core wire that is approximately 50% Nickel and having a coating comprising between approximately 0.3% and approximately 3.0% Magnesium and rare earth metals and oxides that is capable of producing an austenitic weld deposit comprising:
between approximately 54% and approximately 60% Nickel;
between approximately 3.5% and approximately 5.5% Manganese; and
between approximately 0.9% and approximately 1.4% Carbon,
approximately 0.5% Silicon;
less than approximately 0.03% Sulfur;
less than approximately 0.2% Copper;
less than approximately 0.5% Aluminum; and
between approximately 33.0% and approximately 41.5% Iron,
wherein the weld deposit is carbide-free and the Carbon is present in the form of nodular graphite and
wherein the weld deposit is carbide-free in a fusion zone and a mixed zone and throughout the weld structure.