Method and compositions that can be used for sealing and assembling components of a powertrain

1. A polyorganosiloxane composition X that is crosslinkable into elastomer in the presence of moisture provided by ambient air or by prior addition of water, via polycondensation reaction comprising:

A) at least one polyorganosiloxane A comprising at least one alkoxylated group and comprising identical or different siloxyl units, of formula:

(Z) b (R 4 ) a SiO [4−(a+b)]/2   (1)

in which:

the symbol Z =[—(OCH 2 CH 2 ) c —OR 5 ], with c=0 or 1,

a=0, 1, 2 or 3; b=0, 1, 2 or 3, a+b=0, 1, 2 or 3,

the symbol R 4 represents a C 1 to C 13 monovalent hydrocarbon-based radical,

the symbol R 5 represents a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally comprising an ester function, and

with the condition that for at least one siloxyl unit, the index b≧1 such that the polyorganosiloxane A contains at least one alkoxylated group Z,

B) optionally at least one polyalkoxylated silane B of formula:

(R 2 ) z Si(OR 3 )( 4−z )  (2)

in which:

z =0 or 1,

the symbol R 2 represents a C 1 to C 13 monovalent hydrocarbon-based radical, and

the symbols R 3 , which may be identical or different, each represent a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally containing an ester function,

C) at least one acetylene black D whose function is to absorb an oil used in a powertrain,

D) at least one aluminum trihydrate E as mineral filler,

E) at least one adhesion promoter F bearing at least one amine function,

F) a catalytically effective amount of at least one guanidine G as condensation catalyst,

G) optionally at least one unreactive linear polyorganosiloxane H,

H) optionally at least one filler I, different from E, and

I) optionally at least one additive J such as a coloring base, a pigment or a thixotropic agent,

with the additional conditions that

said polyorganosiloxane composition X contains neither any calcium carbonate nor any siloxane containing from 2 to 10 siloxyl units obtained by partial hydrolysis and condensation of a polyalkoxylated silane, and that

the polyorganosiloxane A has a number of units strictly greater than 10, optionally greater than 20 and at most equal to 2000.

2. The polyorganosiloxane composition X as claimed in claim 1 , comprising:

A) at least one polyorganosiloxane A comprising at least one alkoxylated group and comprising identical or different siloxyl units, of formula:

(Z) b (R 4 ) a SiO [4−(a+b)]/2   (1)

in which:

a. the symbol Z =[—(OCH 2 CH 2 ) c —OR 5 ], with c=0 or 1,

b. a=0, 1, 2 or 3; b=0, 1, 2 or 3, a+b=0, 1, 2 or 3,

c. the symbol R 4 represents a C 1 to C 13 monovalent hydrocarbon-based radical,

d. the symbol R 5 represents a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally comprising an ester function, and

e. with the condition that for at least one siloxyl unit, the index b≧1 such that the polyorganosiloxane A contains at least one alkoxylated group Z,

B) at least one polyalkoxylated silane B of formula:

(R 2 ) z Si(OR 3 ) (4−z)   (2)

in which:

z=0 or 1,

the symbol R 2 represents a C 1 to C 13 monovalent hydrocarbon-based radical, and

the symbols R 3 , which may be identical or different, each represent a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally containing an ester function,

C) at least one acetylene black D whose function is to absorb an oil used in a powertrain,

D) at least one aluminum trihydrate E as mineral filler,

E) at least one adhesion promoter F bearing at least one amine function,

F) a catalytically effective amount of at least one guanidine G as condensation catalyst,

G) optionally at least one unreactive linear polyorganosiloxane H,

H) optionally at least one filler I, different from E, and

I) optionally at least one additive J such as a coloring base, a pigment or a thixotropic agent,

with the additional conditions that

said polyorganosiloxane composition X contains neither any calcium carbonate nor any siloxane containing from 2 to 10 siloxyl units obtained by partial hydrolysis and condensation of a polyalkoxylated silane, and that

the polyorganosiloxane A has a number of units strictly greater than 10, optionally greater than 20 and at most equal to 2000.

3. The polyorganosiloxane composition X as claimed in claim 1 , in the form of an RTV-1 one-pack composition whose package is airtight.

4. The polyorganosiloxane composition X as claimed in claim 1 , in which the crosslinkable polyorganosiloxane A is linear and has the structural formula:

in which:

the substituents R1, which may be identical or different, each represent a substituted or unsubstituted aliphatic, cyclanic or aromatic C 1 to C 13 saturated or unsaturated monovalent hydrocarbon-based radical;

the substituents R2, which may be identical or different, each represent a substituted or unsubstituted aliphatic, cyclanic or aromatic C 1 to C 13 saturated or unsaturated monovalent hydrocarbon-based radical;

the substituents R3, which may be identical or different, each represent a linear or branched C 1 to C 6 alkyl radical;

n has a value sufficient to give the polyorganopolysiloxane of formula A a dynamic viscosity at 25° C. ranging from 1000 to 1 000 000 mPa·s; and

the index a is equal to zero or 1 and the index b is equal to zero or 1.

5. The polyorganosiloxane composition X as claimed in claim 1 , in which the polyorganosiloxane A comprising at least one alkoxylated group is obtained by reacting, optionally in situ, in the presence of a catalytically effective amount of at least one functionalization catalyst C:

a) at least one polyorganosiloxane A′ comprising siloxyl units of formula:

(R 1 ) x (OH) y SiO (4−x−y)/2   (4)

in which:

x=0, 1, 2 or 3; y=0, 1, 2 or 3, x+y=0, 1, 2 or 3;

the substituents R 1 , which may be identical or different, each represent a C 1 to C 30 monovalent hydrocarbon-based radical chosen from the group consisting of alkyl, cycloalkyl, aryl; alkaryl and aralkyl radicals, and

at least two siloxyl units comprising a group ≡SiOH are present in the polyorganosiloxane A′, preferably at the chain ends, with

b) at least one polyalkoxylated silane B of formula:

(R 2 ) z Si(OR 3 ) (4−z)   (2)

in which:

z =0 or 1,

the symbol R 2 represents a C 1 to C 13 monovalent hydrocarbon-based radical, and

the symbols R 3 , which may be identical or different, each represent a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally containing an ester function.

6. The polyorganosiloxane composition X as claimed in claim 5 , in which the functionalization catalyst C is lithium hydroxide or potassium hydroxide.

7. The polyorganosiloxane composition X as claimed in claim 1 , in which the condensation catalyst G is a guanidine corresponding to formula (I):

in which:

the radicals R 1 , which may be identical or different, represent, independently of each other, a linear or branched monovalent alkyl group, a cycloalkyl group, a (cycloalkyl)alkyl group, the ring being optionally substituted and possibly comprising at least one heteroatom or a fluoroalkyl group,

the radical R 2 represents a hydrogen atom, a linear or branched monovalent alkyl group, a cycloalkyl group, an alkyl group substituted with a ring that is optionally substituted and that possibly comprises at least one heteroatom, an aromatic group, an arylalkyl group, a fluoroalkyl group, an alkylamine group or an alkylguanidine group,

the radical R 3 represents a linear or branched monovalent alkyl group, a cycloalkyl group, an alkyl group substituted with a ring that is optionally substituted and that possibly comprises at least one heteroatom, an arylalkyl, fluoroalkyl, alkylamine or alkylguanidine group, and

when the radical R 2 is not a hydrogen atom, the radicals R 2 and R 3 may be linked to form a 3-, 4-, 5-, 6- or 7-membered aliphatic ring optionally substituted with one or more substituents.

8. The polyorganosiloxane composition X as claimed in claim 1 , in which the condensation catalyst G is a guanidine of formula:

in which:

the radicals R 1 , R 2 , R 3 , R 4 or R 5 , which may be identical or different, represent, independently of each other, a linear or branched monovalent alkyl group, a cycloalkyl group, a (cycloalkyl)alkyl group, the ring being optionally substituted and possibly comprising at least one heteroatom or a fluoroalkyl group, an aromatic group, an arylalkyl group, a fluoroalkyl group, an alkylamino group or an alkylguanidine group, and

the radicals R 1 , R 2 , R 3 or R 4 may be linked in pairs so as to form a 3-, 4-, 5-, 6- or 7-membered aliphatic ring optionally substituted with one or more substituents.

9. The polyorganosiloxane composition X as claimed in claim 1 , in which at least one filler I is present, optionally a kaolin.

10. The polyorganosiloxane composition X as claimed in claim 1 , comprising:

A) per 100 parts by weight of at least one polyorganosiloxane A comprising at least one alkoxylated group and comprising identical or different siloxyl units, of formula:

(Z) b (R 4 ) a SiO [4−(a+b)]/2   (1)

in which:

the symbol Z =[—(OCH 2 CH 2 ) c —OR 5 ], with c=0 or 1,

a=0, 1, 2 or 3; b=0, 1, 2 or 3, a+b=0, 1, 2 or 3 ,

the symbol R 4 represents a C 1 to C 13 monovalent hydrocarbon-based radical,

the symbol R 5 represents a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally comprising an ester function, and

with the condition that for at least one siloxyl unit, the index b is ≧1 such that the polyorganosiloxane A contains at least one alkoxylated group Z,

B) from 0 to 50 parts by weight of at least one polyalkoxylated silane B of formula

(R 2 ) z Si(OR 3 ) (4−z)   (2)

in which:

z =0 or 1,

the symbol R 2 represents a C 1 to C 13 monovalent hydrocarbon-based radical, and

the symbols R 3 , which may be identical or different, each represent a C 1 to C 6 monovalent hydrocarbon-based radical or an alkoxyalkyl radical optionally containing an ester function,

C) from 0.1 to 50 parts by weight of at least one acetylene black D whose function is to absorb an oil used in a powertrain,

D) from 0.1 to 50 parts by weight of at least one aluminum trihydrate E as mineral filler,

E) from 0.1 to 60 parts by weight of at least one adhesion promoter F bearing at least one amine function,

F) from 0.01 to 50 parts by weight of at least one guanidine G as condensation catalyst,

G) from 0 to 60 parts by weight of at least one nonreactive linear polyorganosiloxane H,

H) from 0 to 250 parts by weight of at least one filler I, different from E, and

I) from 0 to 20 parts by weight of at least one additive J optionally comprising a coloring base, a pigment or a thixotropic agent,

with the additional conditions that

said polyorganosiloxane composition X contains neither any calcium carbonate nor any siloxane containing from 2 to 10 siloxyl units obtained by partial hydrolysis and condensation of a polyalkoxylated silane, and that

the polyorganosiloxane A has a number of units strictly greater than 10, optionally greater than 20 and at most equal to 2000.

11. An elastomer obtained by crosslinking, in the presence of moisture provided by ambient air or by prior addition of water, of the polyorganosiloxane composition X as defined according to claim 1 .

12. A polyorganosiloxane composition X as defined according to claim 1 , capable of being used for preparing one or more silicone leakproofing seals which have good resistance to aging in one or more fluids used in a powertrain.

13. A process for sealing and assembling at least one component of a powertrain, comprising:

a) preparing a polyorganosiloxane composition X as defined according to claim 1 ,

b) said polyorganosiloxane composition X is applied to at least one zone of contact of said component continuously or discontinuously and optionally in the form of a bead,

c) said polyorganosiloxane composition X is left to crosslink into silicone elastomer in the presence of moisture provided by ambient air or by prior addition of water so as to form a leakproofing seal, and

d) said component is assembled with another component of the powertrain so that the seal formed ensures assembly and leakproofing between the two components of the powertrain.