Aqueous slurry for making a powder of hard material
An aqueous slurry that is useful upon being spray dried for the formation of a powder of hard material. The aqueous slurry includes starting powder components of the hard material. The slurry further includes an oxidation inhibitor, a surfactant in an amount between about 0.05 weight percent and about 0.30 weight percent of the weight of the starting powder components of the hard material, a binder, a defoamer and water in an between about 15 weight percent and about 30 weight percent of the weight of the weight of the starting powder components of the hard material. The aqueous slurry has a percent solids value that is between about 70 percent and about 85 percent.
1. An aqueous slurry useful upon being spray dried for the formation of a powder of hard material, the aqueous slurry comprising:
starting powder components of the hard material;
an oxidation inhibitor in an amount between about 0.2 weight percent and about 0.5 weight percent based on weight of the starting powder components of the hard material;
a surfactant in an amount between about 0.05 weight percent and about 0.30 weight percent of the weight of the starting powder components of the hard material;
a binder in an amount between about 1.2 weight percent and about 4.0 weight percent of the weight of the starting powder components of the hard material;
a defoamer in an amount between about 0.05 weight percent and about 0.35 weight percent of the weight of the starting powder components of the hard material; and water in an amount between about 15 weight percent and about 30 weight percent of the weight of the starting powder components of the hard material; and
the aqueous slurry having a percent solids between about 70 percent and about 85 percent wherein the percent solids comprises a quotient in percent of the weight of the starting powder components of the hard material divided by the sum of the weight of the starting powder components of the hard material and the weight of the water.
2. The aqueous slurry according to claim 1 wherein the oxidation inhibitor comprises aqueous amines or a mixture of aqueous amines and vinyl polymers.
3. The aqueous slurry according to claim 1 wherein the surfactant comprises polyoxyethylene (5) soyaalkylamine.
4. The aqueous slurry according to claim 3 wherein the polyoxyethylene (5) soyaalkylamine is present in an amount between about 0.075 weight percent and about 0.25 weight percent of the weight of the starting powder components of the hard material.
5. The aqueous slurry according to claim 3 wherein the polyoxyethylene (5) soyaalkylamine is present in an amount equal to about 0.15 weight percent of the weight of the starting powder components of the hard material.
6. The aqueous slurry according to claim 1 wherein the binder comprising a wax dispersion.
7. The aqueous slurry according to claim 1 wherein the defoamer comprises alkylpolyalkyleneglycolether.
8. The aqueous slurry according to claim 1 wherein the starting powder components comprises a hard metal powder comprising one or more powders of carbides, nitrides and carbonitrides of the Group IVB, Group VB and Group VIB transition metals of the Periodic Table and binder metals comprising Cobalt, Nickel, Iron, Ruthenium, Manganese, Silicon, Aluminum and Copper and their alloys.
9. The aqueous slurry according to claim 8 wherein the starting powder components of the hard material comprises tungsten carbide powder and cobalt powder, and the tungsten carbide powder being present in an amount greater than 50 weight percent of the starting powder components of the hard material, and the cobalt powder being present in up to 50 weight percent of the starting powder components of the hard material.
10. The aqueous slurry according to claim 9 wherein the tungsten carbide powder being present in an amount between 90 weight percent and about 96 weight percent of the starting powder components of the hard material and the cobalt powder being present in an amount between about 4 weight percent and about 10 weight percent of the starting powder components of the hard material.