Temperature stable solid electrolytic capacitor
A capacitor whose electrical properties can be stable under a variety of different conditions is provided. The solid electrolyte of the capacitor is formed from a combination of an in situ polymerized conductive polymer and a hydroxy-functional nonionic polymer. One benefit of such an in situ polymerized conductive polymer is that it does not require the use of polymeric counterions (e.g., polystyrenesulfonic anion) to compensate for charge, as with conventional particle dispersions, which tend to result in ionic polarization and instable electrical properties, particularly at the low temperatures noted above. Further, it is believed that hydroxy-functional nonionic polymers can improve the degree of contact between the polymer and the surface of the internal dielectric, which unexpectedly increases the capacitance performance and reduces ESR.
1. A solid electrolytic capacitor comprising:
a sintered porous anode;
a dielectric layer that overlies the anode body; and
a solid electrolyte overlying the dielectric layer, wherein the solid electrolyte comprises a first layer that overlies the dielectric layer and includes an in situ polymerized conductive polymer and a second layer that overlies the first layer, wherein the second layer includes a plurality of pre-polymerized conductive polymer particles and a separate hydroxy-functional nonionic polymer.
2. The solid electrolytic capacitor of claim 1 , wherein the in situ polymerized conductive polymer and the pre-polymerized conductive polymer particles include is a substituted polythiophene.
3. The solid electrolytic capacitor of claim 1 , wherein the hydroxy-functional nonionic polymer has a molecular weight of from about 300 to about 1,200 grams per mole.
4. The solid electrolytic capacitor of claim 1 , wherein the hydroxy-functional polymer is a polyalkylene ether.
5. The solid electrolytic capacitor of claim 4 , wherein the polyalkylene ether is a polyalkylene glycol.
6. The solid electrolytic capacitor of claim 1 , wherein the hydroxy-functional polymer is an ethoxylated alkylphenol, ethoxylated or propoxylated C 6 -C 24 fatty alcohol, polyoxyethylene glycol alkyl ether, polyoxyethylene glycol alkyl phenol ether, polyoxyethylene glycol ester of a C 8 -C 24 fatty acid, polyoxyethylene glycol ether of a C 8 -C 24 fatty acid, block copolymer of polyethylene glycol and polypropylene glycol, or a combination thereof.
7. The solid electrolytic capacitor of claim 2 , wherein the substituted polythiophene is poly(3,4-ethylenedioxythiophene).
8. The solid electrolytic capacitor of claim 1 , wherein the particles contain a monomeric or polymeric counteranion.
9. The solid electrolytic capacitor of claim 1 , further comprising an external polymer coating that overlies the solid electrolyte, wherein the external polymer coating contains a plurality of pre-polymerized conductive polymer particles.
10. The solid electrolytic capacitor of claim 9 , wherein the external polymer coating contains a first layer that overlies the solid electrolyte and a second layer that overlies the first layer, wherein the first layer contains a crosslinking agent and the second layer contains the pre-polymerized conductive polymer particles.
11. The solid electrolytic capacitor of claim 1 , further comprising an anode termination that is electrically connected to the anode and a cathode termination that is electrically connected to the solid electrolyte.
12. The solid electrolytic capacitor of claim 1 , wherein the capacitor exhibits an equivalence series resistance of about 100 mohms or less at a temperature of −55° C. and an operating frequency of 100 kHz.
13. A method for forming a solid electrolytic capacitor, the method comprising:
anodically oxidizing a sintered porous anode to form a dielectric layer that overlies the anode;
forming a first layer of a solid electrolyte over the dielectric layer by a process that includes chemically polymerizing a monomer in situ to form a conductive polymer, and thereafter
forming a second layer that overlies the first layer by applying a dispersion that includes a plurality of pre-polymerized conductive polymer particles and a separate hydroxy-functional nonionic polymer.
14. The method of claim 13 , wherein the in situ polymerized conductive polymer and the pre-polymerized conductive polymer particles include is a substituted polythiophene.
15. The method of claim 13 , wherein the hydroxy-functional nonionic polymer has a molecular weight of from about 300 to about 1,200 grams per mole.
16. The method of claim 13 , wherein the hydroxy-functional nonionic polymer is a polyalkylene ether.
17. The solid electrolytic capacitor of claim 1 , wherein the hydroxy-functional nonionic polymer constitutes about 2 wt. % or less of the solid electrolyte.
18. The solid electrolytic capacitor of claim 1 , wherein the concentration of hydroxy-functional nonionic polymers in the first layer is about 2 wt. % or less.