Cathode material for lithium secondary battery, and method of producing said cathode material

1. A cathode material for a lithium secondary battery, comprising:

a fibrous carbon; and

a plurality of cathode active material particles composed of olivine-type LiMPO 4 , wherein M represents one or more kinds of elements selected from Fe, Mn, Ni, and Co,

wherein the cathode active material particles are directly bonded to the surface of the fibrous carbon, and

the cathode active material particles are not bonded by a carbon layer which is not a structure of the fibrous carbon,

wherein a surface except a bonding surface with the fibrous carbon in a surface of the cathode active material particles, is coated with carbon.

2. The cathode material for a lithium secondary battery according to claim 1 ,

wherein one or more kinds of metals selected from Co, Ti, V, Cr, Mn, W, Mo, Fe, Cu, Al, V, Nb, and Ta, or one or more kinds of oxides of the metals are carried on the surface of the fibrous carbon, and the cathode active material particles are bonded to the surface at a position at which the metals or metal oxides are carried.

3. The cathode material for a lithium secondary battery according to claim 1 ,

wherein the amount of the fibrous carbon is in a range of 0.5% by mass to 10% by mass in the cathode material.

4. The cathode material for a lithium secondary battery according to claim 1 ,

wherein an average fiber length of the fibrous carbon is in a range of 1 μm to 100 μm.

5. The cathode material for a lithium secondary battery according to claim 4 ,

wherein an aspect ratio (fiber length/fiber diameter), which is a ratio of a fiber length to a fiber diameter of the fibrous carbon, is in a range of 5 to 1000.

6. The cathode material for a lithium secondary battery according to claim 1 ,

wherein an average particle size of the cathode active material particles is in a range of 20 nm to 200 nm.

7. The cathode material for a lithium secondary battery according to claim 1 ,

wherein one or two kinds of elements selected from Nb and V are contained in LiMPO 4 .

8. A method of producing the cathode material for a lithium secondary battery according to claim 1 , the method comprising:

carrying out a conversion reaction into olivine-type LiMPO 4 at 100° C. or higher by using a Li source, an M source, and a phosphoric acid source as a raw material under the presence of a polar solvent in which fibrous carbon is mixed to allow a plurality of cathode active material particles composed of the LiMPO 4 to grow on a surface of the fibrous carbon.

9. The method of producing a cathode material for a lithium secondary battery according to claim 8 , further comprising:

preparing a first raw material liquid comprising any one kind of source selected from the lithium source, the M source, and the phosphoric acid source, and the polar solvent, and a second raw material liquid comprising the remainder which is not contained in the first raw material liquid among the lithium source, the M source, and the phosphoric acid source, and the polar solvent;

adding the fibrous carbon to one or both of the first raw material liquid and the second raw material liquid in advance, or adding the fibrous carbon when the first raw material liquid and the second raw material liquid are mixed; and

mixing the first raw material liquid and the second raw material liquid to allow the conversion reaction to occur.

10. The method of producing a cathode material for a lithium secondary battery according to claim 8 ,

wherein the conversion reaction is carried out under conditions of retention at a temperature of 100° C. to 160° C. and a pressure of 0.1 MPa to 0.6 MPa for 30 minutes to 30 hours, and then retention at a temperature of 180° C. to 260° C. and a pressure of 1.0 MPa to 4.7 MPa for 30 minutes to 30 hours.

11. The method of producing a cathode material for a lithium secondary battery according to claim 8 ,

wherein as the fibrous carbon, fibrous carbon in which one or more kinds of metals selected from Co, Ti, V, Cr, Mn, W, Mo, Fe, Cu, Al, V, Nb, and Ta, or one or more kinds of oxides of the metals are carried on the surface is used.

12. The method of producing a cathode material for a lithium secondary battery according to claim 8 ,

a material comprising Nb or V is added to the raw material.

13. The method of producing a cathode material for a lithium secondary battery according to claim 8 ,

wherein the lithium source is lithium hydroxide, the M source is a sulfate of one or more kinds of metals selected from Fe, Mn, Ni, and Co, and the phosphoric acid source is phosphoric acid.

14. The method of producing a cathode material for a lithium secondary battery according to claim 8 ,

wherein lithium phosphate is used as the lithium source and the phosphoric acid source.