Granules comprising bitumen and a thermoplastic polyurethane elastomer, method for its preparation and its uses
Disclosed are granules comprising an elastomeric polyurethane and bitumen, processes for preparing the granules in an extruder and to their use for preparing a bituminous binder, which may especially be used for producing prefabricated sealing membranes by depositing said bituminous binder onto a fibrous support.
1. A granule, wherein said granule comprises a thermoplastic elastomeric polyurethane and bitumen, wherein said thermoplastic elastomeric polyurethane has a glass transition temperature (Tg) of between −60° C. and 0° C. and is obtained by reaction between:
a polyol having a functionality of between 1.75 and 2.2, and a molar mass of between 500 and 6000 g/mol;
a diisocyanate; and
a chain-extending diol with a molar mass of less than 500 g/mol;
with an NCO/OH ratio of between 0.9 and 1.02.
2. A granule according to claim 1 , wherein said granule comprises:
5% to 70% by weight of bitumen relative to the weight of the granule;
95% to 30% by weight of thermoplastic elastomeric polyurethane relative to the weight of the granule.
3. A granule according to claim 1 , wherein the polyol is chosen from a polyether polyol, a polyester polyol, a polycarbonate polyol, a polyolefin polyol, a polyol based on plant oil, and mixtures thereof.
4. A granule according to claim 1 , wherein the diisocyanate is chosen from aromatic, aliphatic and cycloaliphatic diisocyanates, and mixtures thereof.
5. A granule according to claim 1 , wherein said granule has a melting point of between 100 and 200° C.
6. A granule according to claim 1 , wherein said granule has a melt flow index (190° C./3.8 kg) of between 50 and 500.
7. A granule according to claim 1 , wherein the thermoplastic elastomeric polyurethane is synthesized by reactive extrusion in the presence of bitumen.
8. A process for preparing a granule of thermoplastic elastomeric polyurethane dispersed in bitumen, wherein said polyurethane has a glass transition temperature (Tg) of between −60° C. and 0° C. and is obtained by polymerization reaction between:
a polyol having a functionality of between 1.75 and 2.2, and a molar mass of between 500 and 6000 g/mol;
a diisocyanate; and
a chain-extending diol with a molar mass of less than 500 g/mol;
with an NCO/OH ratio of between 0.9 and 1.02;
said polymerization reaction being performed in an extruder in the presence of bitumen.
9. A process according to claim 8 , wherein said granule comprises:
5% to 70% by weight of bitumen relative to the weight of the granule;
95% to 30% by weight of thermoplastic elastomeric polyurethane relative to the weight of the granule.
10. A process according to claim 8 , wherein said process comprises the following steps:
introduction of the polyol, the diisocyanate, the chain-extending diol into an extruder;
introduction of the bitumen into the extruder;
chopping of the extrudate into granules at the extruder outlet.
11. A process according to claim 8 , wherein said process comprises the following steps:
preparation of a prepolymer by reaction between the polyol and the diisocyanate;
introduction of the prepolymer, the chain-extending diol into an extruder;
introduction of the bitumen into the extruder;
chopping of the extrudate into granules at the extruder outlet.
12. A process for preparing a bituminous binder, comprising incorporating the granules of claim 1 into a composition comprising liquid bitumen.
13. A process for preparing a prefabricated sealing membrane, comprising depositing the bituminous binder prepared according to claim 12 onto a fibrous support.
14. A process for preparing a bituminous binder, comprising incorporating granules prepared according to claim 8 into a composition comprising liquid bitumen.
15. A process for preparing a prefabricated sealing membrane, comprising depositing the bituminous binder prepared according to claim 14 onto a fibrous support.