Multilayer ceramic capacitor and method for producing the same
A dielectric ceramic that forms dielectric ceramic layers of a multilayer ceramic capacitor contains a Ba and Ti containing perovskite compound, Ca, R (R denotes a rare earth element, such as La), M (M denotes Mn or the like), and Si. The Ca content ranges from 0.5 to 2.5 molar parts, the R content ranges from 0.5 to 4 molar parts, the M content ranges from 0.5 to 2 molar parts, and the Si content ranges from 1 to 4 molar parts, based on 100 molar parts of Ti. In perovskite crystal grains, the Ca diffusion depth is 10% or less of the average grain size of the crystal grains, and the Ca concentration in a Ca diffusion region is 0.2 to 5 molar parts higher than the Ca concentration near the center of each of the crystal grains.
1. A multilayer ceramic capacitor comprising:
a multilayer body including a plurality of stacked dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers comprising a dielectric ceramic containing crystal grains and crystal grain boundaries; and
an outer electrode disposed on a surface of the multilayer body and electrically connected to specific internal electrodes thereamong,
wherein the multilayer body contains
a perovskite compound containing Ba and Ti, and
Ca, R, M, and Si,
wherein R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and
M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W,
the multilayer body contains, with respect to 100 molar parts of Ti,
0.5 molar parts to 2.5 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound,
wherein, when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.
2. The multilayer ceramic capacitor according to claim 1 , wherein R is diffused in the Ca diffusion depth region.
3. The multilayer ceramic capacitor according to claim 1 , wherein each of the dielectric ceramic layers has a thickness of 0.8 μm or less on average.
4. A multilayer ceramic capacitor comprising:
a multilayer body including a plurality of stacked dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
an outer electrode disposed on a surface of the multilayer body and electrically connected to specific internal electrodes thereamong,
wherein the multilayer body contains
a perovskite compound containing Ba and Ti, and
Ca, R, M, and Si,
wherein R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and
M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W,
a solution of the multilayer body contains, with respect to 100 molar parts of Ti,
0.5 molar parts to 2.5 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
wherein, when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.
5. The multilayer ceramic capacitor according to claim 4 , wherein R is diffused in the Ca diffusion depth region.
6. The multilayer ceramic capacitor according to claim 4 , wherein each of the dielectric ceramic layers has a thickness of 0.8 μm or less on average.
7. A multilayer ceramic capacitor comprising:
a multilayer body including a plurality of stacked dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
an outer electrode disposed on a surface of the multilayer body and electrically connected to specific internal electrodes thereamong,
wherein the dielectric ceramic layers contain
a perovskite compound containing Ba and Ti, and
Ca, R, M, and Si,
wherein R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and
M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W,
the dielectric ceramic layers contain, with respect to 100 molar parts of Ti,
0.5 molar parts to 2.5 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.
8. The multilayer ceramic capacitor according to claim 7 , wherein R is diffused in the Ca diffusion depth region.
9. The multilayer ceramic capacitor according to claim 7 , wherein each of the dielectric ceramic layers has a thickness of 0.8 μm or less on average.
10. A multilayer ceramic capacitor comprising:
a multilayer body including a plurality of stacked dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
an outer electrode disposed on a surface of the multilayer body and electrically connected to specific internal electrodes thereamong,
wherein the multilayer body contains
a perovskite compound containing Ba, Ca, and Ti, and
Ca, R, M, and Si,
wherein R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and
M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W,
the multilayer body contains, with respect to 100 molar parts of Ti,
2.5 molar parts to 15 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
wherein, when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2molar parts to 5 molar parts.
11. The multilayer ceramic capacitor according to claim 10 , wherein R is diffused in the Ca diffusion depth region.
12. The multilayer ceramic capacitor according to claim 10 , wherein each of the dielectric ceramic layers has a thickness of 0.8 μm or less on average.
13. A multilayer ceramic capacitor comprising:
a multilayer body including a plurality of stacked dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
an outer electrode disposed on a surface of the multilayer body and electrically connected to specific internal electrodes thereamong,
wherein the multilayer body contains
a perovskite compound containing Ba, Ca, and Ti, and
Ca, R, M, and Si,
wherein R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and
M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W,
a solution of the multilayer body contains, with respect to 100 molar parts of Ti,
2.5 molar parts to 15 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
wherein, when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.
14. The multilayer ceramic capacitor according to claim 13 , wherein R is diffused in the Ca diffusion depth region.
15. The multilayer ceramic capacitor according to claim 13 , wherein each of the dielectric ceramic layers has a thickness of 0.8 μm or less on average.
16. A multilayer ceramic capacitor comprising:
a multilayer body including a plurality of stacked dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
an outer electrode disposed on a surface of the multilayer body and electrically connected to specific internal electrodes thereamong,
wherein the dielectric ceramic layers contain
a perovskite compound containing Ba, Ca, and Ti, and
Ca, R, M, and Si,
wherein R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and
M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W,
the dielectric ceramic layers contain, with respect to 100 molar parts of Ti,
2.5 molar parts to 15 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.
17. The multilayer ceramic capacitor according to claim 16 , wherein R is diffused in the Ca diffusion depth region.
18. The multilayer ceramic capacitor according to claim 16 , wherein each of the dielectric ceramic layers has a thickness of 0.8 μm or less on average.
19. A method for producing a multilayer ceramic capacitor, the method comprising:
preparing a ceramic slurry containing a main component powder, a Ca compound, an R compound, an M compound, and a Si compound, the main component powder being composed mainly of a perovskite compound containing Ba and Ti, R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W;
forming a ceramic green sheet from the ceramic slurry;
forming an internal electrode on the ceramic green sheet;
stacking a plurality of the ceramic green sheets including the ceramic green sheet on which the internal electrode is formed to form a green multilayer body;
firing the green multilayer body to form a multilayer body including a plurality of dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
forming an outer electrode on a surface of the multilayer body such that the outer electrode is electrically connected to specific internal electrodes thereamong,
wherein the ceramic slurry contains, with respect to 100 molar parts of Ti,
0.5 molar parts to 2.5 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
wherein, when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.
20. A method for producing a multilayer ceramic capacitor, the method comprising:
preparing a ceramic slurry containing a main component powder, a Ca compound, an R compound, an M compound, and a Si compound, the main component powder being composed mainly of a perovskite compound containing Ba, Ca, and Ti, R is at least one of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Y, and M is at least one of Mn, Co, Fe, Cr, Cu, Mg, Al, V, Mo, and W;
forming a ceramic green sheet from the ceramic slurry;
forming an internal electrode on the ceramic green sheet;
stacking a plurality of the ceramic green sheets including the ceramic green sheet on which the internal electrode is formed to form a green multilayer body;
firing the green multilayer body to form a multilayer body including a plurality of dielectric ceramic layers and a plurality of internal electrodes disposed along a plurality of interfaces between the dielectric ceramic layers, the dielectric ceramic layers being formed of a dielectric ceramic containing crystal grains and crystal grain boundaries; and
forming an outer electrode on a surface of the multilayer body such that the outer electrode is electrically connected to specific internal electrodes thereamong,
wherein the ceramic slurry contains, with respect to 100 molar parts of Ti,
2.5 molar parts to 15 molar parts of Ca,
0.5 molar parts to 4 molar parts of R,
0.5 molar parts to 2 molar parts of M, and
1 molar parts to 4 molar parts of Si,
the crystal grains include perovskite crystal grains composed mainly of the perovskite compound, and
wherein, when a Ca concentration in the perovskite crystal grains is represented by a relative Ca concentration with respect to 100 molar parts of Ti at a point of measurement,
the crystal grains have a Ca diffusion depth region within 10% of an average grain size of the crystal grains and that extends from the crystal grain boundary toward the center of the crystal grain, and
a difference between an average of the Ca concentration in the entirety of the Ca diffusion depth region and the Ca concentration at the center of the crystal grain ranges from 0.2 molar parts to 5 molar parts.