Silica composite particles and method of preparing the same
A method of preparing silica composite particles includes preparing an alkali catalyst solution containing an alkali catalyst at a concentration of from 0.6 mol/L to 0.85 mol/L, in a solvent containing alcohol; and supplying, into the alkali catalyst solution, (i) a mixed solution of tetraalkoxysilane and an organic titanium compound in which an organic group is coupled to a titanium atom through oxygen, and (ii) an alkali catalyst. The mixed solution is supplied at a supply amount of from 0.001 mol/(mol·min) to 0.01 mol/(mol·min) relative to the alcohol, and the alkali catalyst is supplied at a supply amount of from 0.1 mol to 0.4 mol, relative to 1 mol of a total supply amount of the tetraalkoxysilane and the organic titanium compound supplied per one minute.
1. A method of preparing silica composite particles comprising:
preparing an alkali catalyst solution containing an alkali catalyst at a concentration of from 0.6 mol/L to 0.85 mol/L, in a solvent containing alcohol; and
supplying, into the alkali catalyst solution:
a mixed solution of tetraalkoxysilane and an organic titanium compound in which an organic group is coupled to a titanium atom through oxygen at a supply amount of from 0.001 mol/(mol·min) to 0.01 mol/(mol·min) relative to the alcohol, and
an alkali catalyst at a supply amount of from 0.1 mol to 0.4 mol, relative to 1 mol of a total supply amount of the tetraalkoxysilane and the organic titanium compound supplied per one minute.
2. The method of preparing silica composite particles according to claim 1 , wherein the concentration of the alkali catalyst is from 0.63 mol/L to 0.78 mol/L.
3. The method of preparing silica composite particles according to claim 1 , wherein the concentration of the alkali catalyst is from 0.66 mol/L to 0.75 mol/L.
4. The method of preparing silica composite particles according to claim 1 , wherein the supply amount of the mixed solution of the tetraalkoxysilane and the organic titanium compound is from 0.002 mol/(mol·min) to 0.009 mol/(mol·min) relative to the alcohol of the alkali catalyst solution.
5. The method of preparing silica composite particles according to claim 1 , wherein the supply amount of the mixed solution of the tetraalkoxysilane and the organic titanium compound is from 0.003 mol/(mol·min) to 0.008 mol/(mol·min) relative to the alcohol of the alkali catalyst solution.
6. The method of preparing silica composite particles according to claim 1 , wherein the supply amount of the alkali catalyst is from 0.14 mol to 0.35 mol relative to 1 mol of the total supply amount of the tetraalkoxysilane and the organic titanium compound supplied per one minute.
7. The method of preparing silica composite particles according to claim 1 , wherein the supply amount of the alkali catalyst is from 0.18 mol to 0.30 mol relative to 1 mol of the total supply amount of the tetraalkoxysilane and the organic titanium compound supplied per one minute.