Wear resistant steel having excellent toughness and weldability
Provided is a wear resistant steel including 2.6 wt % to 4.5 wt % of manganese (Mn), carbon (C) satisfying (6-Mn)/50≦C≦(10-Mn)/50, 0.05 wt % to 1.0 wt % of silicon (Si), and iron (Fe) as well as other unavoidable impurities as a remainder, wherein a Brinell hardness of a surface portion is in a range of 360 to 440. The wear resistant steel further includes at least one component selected from the group consisting of 0.1 wt % or less (excluding 0 wt %) of niobium (Nb), 0.1 wt % or less (excluding 0 wt %) of vanadium (V), 0.1 wt % or less (excluding 0 wt %) of titanium (Ti), and 0.02 wt % or less (excluding 0 wt %) of boron (B) to complement the performance thereof. The wear resistant steel is characterized in that a microstructure includes martensite in an amount of 90% or more, and an average packet diameter of the martensite is 20 μm or less.
1. A wear resistant steel comprising:
2.6 wt % to 4.5 wt % of manganese (Mn);
carbon (C) satisfying (6-Mn)/50≦C≦(10-Mn)/50;
0.05 wt % to 1.0 wt % of silicon (Si); and
iron (Fe) as well as other unavoidable impurities as a remainder,
wherein a microstructure of the wear resistant steel comprises martensite in an amount of 90% or more (including 100%) and bainite in an amount of 10% or less (including 0%),
wherein the microstructure excludes ferrite, and
wherein a Brinell hardness of a surface portion is in a range of 360 to 440.
2. The wear resistant steel of claim 1 , further comprising at least one component selected from the group consisting of 0.1 wt % or less (excluding 0 wt %) of niobium (Nb), 0.1 wt % or less (excluding 0 wt %) of vanadium (V), 0.1 wt % or less (excluding 0 wt %) of titanium (Ti), and 0.02 wt % or less (excluding 0 wt %) of boron (B).
3. The wear resistant steel of claim 1 , wherein an average packet diameter of the martensite is 20 μm or less.
4. The wear resistant steel of claim 1 , wherein the microstructure consists of the marteniste and the bainite in a total amount of 100%.