A method to prepare a self-decontaminating surface, where that method includes disposing a first coating on a surface, where that first coating comprises an organosilane, and disposing a second coating over the first coating, where the second coating comprises TiO 2 .
1. A method of forming a self-decontaminating coating on a surface, comprising the steps of:
(1) coating a surface with an aqueous mixture comprising 3-(trimethoxysilyl)propyldimethyloctadecyl ammonium chloride; and
(2) subsequently coating the surface with an aqueous colloidal suspension of TiO 2 thus forming said self-decontaminating coating on said surface,
wherein said self-decontaminating coating exhibits a reduction in bacteria after initial inoculation of the coating with bacteria.
2. The method of claim 1 , wherein said surface comprises formica.
3. The method of claim 1 , wherein said aqueous colloidal suspension further comprises an oxidizable pigment.
4. The method of claim 3 , wherein said pigment is oxidizable by TiO 2 .
5. The method of claim 3 , wherein said pigment comprises methylene blue.
6. The method of claim 1 , wherein step (2) follows step (1) by about 15 minutes.
7. The method of claim 1 , wherein said aqueous colloidal suspension of TiO 2 comprises a 3 weight percent TiO 2 suspension in water.
8. The method of claim 1 , wherein said aqueous mixture comprises a 3.6 weight percent solution of 3-(trimethoxysilyl)propyldimethyloctadecyl ammonium chloride in water.
9. The method of claim 1 , wherein said reduction in bacteria comprises an about 2.3 log reduction in Methicillin Resistant Staphylococcus Aureus (MRSA) after initial inoculation of the treated surface with MRSA.
10. The method of claim 1 , wherein said reduction in bacteria comprises an about 2.3 log reduction in Methicillin Resistant Staphylococcus Aureus (MRSA) about 3 hours after initial inoculation of the treated surface with MRSA.