Lithium disilicate apatite glass-ceramic
Lithium disilicate apatite glass-ceramics are described which are characterized by a high chemical stability and can therefore be used in particular as restoration material in dentistry.
1. Lithium disilicate apatite glass-ceramic, which comprises lithium disilicate as main crystal phase and apatite as further crystal phase and which comprises 3.0 to 7.0 wt.-% K 2 O.
2. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 60.0 to 74.0 wt.-% SiO 2 .
3. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 10.0 to 20.0 wt.-% Li 2 O.
4. Lithium disilicate apatite glass-ceramic according to claim 1 , which contains 3.0 to 7.0 wt.-% P 2 O 5 .
5. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 0 to 5.0 wt.-% CaO and 0 to 4.0 wt.-% SrO, wherein the combined amount of CaO and SrO is 1.5 to 5.5 wt.-%.
6. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 0.1 to 1.0 wt.-% F.
7. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 2.0 to 7.0 wt.-% oxide of trivalent elements and/or further oxide of tetravalent elements.
8. Lithium disilicate apatite glass-ceramic according to claim 7 , wherein the oxide of trivalent elements is selected from the group of Al 2 O 3 , Y 2 O 3 , La 2 O 3 and mixtures thereof.
9. Lithium disilicate apatite glass-ceramic according to claim 7 , wherein the further oxide of tetravalent elements is selected from the group of ZrO 2 , TiO 2 , GeO 2 and mixtures thereof.
10. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises at least one of the following components:
Component
wt.-%
SiO 2
60.0 to 74.0
Li 2 O
10.0 to 20.0
P 2 O 5
3.0 to 7.0
K 2 O
3.0 to 7.0
CaO
0 to 5.0
SrO
0 to 4.0
F
0.1 to 1.0
Oxide of trivalent elements and/or further
2.0 to 7.0
oxide of tetravalent elements
wherein
CaO + SrO is
1.5 to 5.5.
11. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises fluoroapatite as apatite.
12. Lithium disilicate apatite glass ceramic which comprises lithium disilicate as main crystal phase and apatite as further crystal phase, which comprises 3.0 to 7.0 wt.-% K 2 O, and which comprises more than 20 vol.-% lithium disilicate crystals.
13. Lithium metasilicate glass-ceramic, which comprises lithium metasilicate as main crystal phase and apatite as further crystal phase and which comprises 3.0 to 7.0 wt.-% K 2 O.
14. Glass-ceramic according to claim 1 , wherein the glass-ceramic is present in the form of a powder, a granulate, a blank or a dental restoration.
15. Process for the preparation of the glass-ceramic according to claim 1 , wherein a starting glass or a lithium metasilicate glass-ceramic is subjected to at least one heat treatment in the range of from 430° to 1000° C.
16. Process according to claim 15 , wherein
(a) the starting glass is subjected to a heat treatment at a temperature of from 430 to 550° C. in order to form starting glass with nuclei, and
(b) the starting glass with nuclei is subjected to a heat treatment at a temperature of from 750 to 950° C. in order to form the lithium disilicate apatite glass-ceramic.
17. Process of using the glass-ceramic according to claim 1 , as dental material comprising coating dental restorations and preparing dental restorations.
18. Process of using the glass-ceramic according to claim 17 , wherein the process comprises pressing or machining, the shape of the desired dental restoration, bridge, inlay, onlay, veneer, abutment, partial crown, crown or shell.
19. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 3.5 to 6.0 wt.-% K 2 O.
20. Lithium disilicate apatite glass-ceramic according to claim 2 , which comprises 63.0 to 71.0 wt.-% SiO 2 .
21. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 11.0 to 19.0 wt.-% Li 2 O.
22. Lithium disilicate apatite glass-ceramic according to claim 1 , which contains 4.0 to 6.0 wt.-% P 2 O 5 .
23. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 0 to 4.5 wt.-% CaO and 0 to 3.5 wt.-% SrO, wherein the combined amount of CaO and SrO is 1.5 to 5.5 wt.-%.
24. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 0.2 to 0.5 wt.-% F.
25. Lithium disilicate apatite glass-ceramic according to claim 1 , which comprises 3.0 to 6.0 wt.-% oxide of trivalent elements and/or further oxide of tetravalent elements.
26. Lithium disilicate apatite glass-ceramic according to claim 7 , wherein the oxide of trivalent elements is selected from the group of Al 2 O 3 , Y 2 O 3 , La 2 O 3 and mixtures thereof.
27. Lithium disilicate apatite glass ceramic according to claim 1 , which comprises more than 25 vol.-% lithium disilicate crystals.
28. Lithium disilicate apatite glass ceramic according to claim 1 , which comprises more than 30 vol.-% lithium disilicate crystals.
29. Lithium metasilicate glass-ceramic according to claim 13 , wherein the lithium metasilicate glass-ceramic is present in the form of a powder, a granulate, a blank or a dental restoration.
30. Process of using the lithium metasilicate glass-ceramic according to claim 13 as dental material comprising coating dental restorations and preparing of dental restorations.