Process for producing polyvinyl alcohol articles
The present invention provides a process for modifying the surface of a polyvinyl alcohol film or fabric by applying heat and pressure to the film or fabric to increase the moisture on the surface which is held by the fabric and to coalesce the surface fibers and reduce the porosity of the surface.
1. A process for producing a polyvinyl alcohol fabric having at least one surface that is coalesced and has a reduced porosity which comprises the step of applying heat and pressure to a polyvinyl alcohol fabric having a moisture content of at least 5-10% by weight so as to increase the moisture at the surface and cause surface fibers on a surface of the fabric to coalesce and to lower its surface porosity to a desired level, wherein the initial fabric is passed through a pair of calendar rolls, wherein one of the rolls is a heated roller and an opposed one of the rolls is an unheated roller having a surface coating of a high melting polymer film.
2. The process of claim 1 wherein both surfaces of the fiber have been treated to form a coalesced and reduced porosity surface.
3. The process of claim 1 wherein the unheated calendar roll is relatively softer than the heated calendar roll.
4. The process of claim 1 wherein the polymer film is selected from the group consisting of polyamide, polytetrafluoroethylene, polyurethane and silicone rubber.
5. The process of claim 1 wherein the fabric is treated with an additive on the surface to be coalesced.
6. The process of claim 5 where the additive is selected from the group consisting of an anti-static agent, water repellant, and a dye.
7. The process of claim 1 wherein the moisture content of the initial fabric is between 5 to 15% by weight.
8. The process of claim 1 wherein the fabric is a laminate of another thermoplastic.
9. The process of claim 8 wherein the other thermoplastic comprises a polyolefin.
10. The process of claim 9 wherein said polyolefin is polyethylene.
11. A polyvinyl alcohol fabric having at least one coalesced surface with a reduced porosity prepared by the process of claim 1 .
12. The polyvinyl alcohol fabric of claim 11 which comprises a water repellant coating on the coalesced surface.
13. The process of claim 1 wherein the polyvinyl alcohol in the fabric has 98 percent or greater hydrolyzed acetyl groups.
14. The process of claim 1 wherein the heated roll is heated to a temperature of between about 120 to 190° C., and wherein the pair of opposed rolls apply the heat and pressure to the polyvinyl alcohol fabric.
15. The process of claim 14 wherein the unheated roll has a relatively softer surface than the heated roll.
16. The process of claim 1 further comprising after applying heat and pressure, passing the fabric through a further pair of opposed rolls, wherein one or both of the rolls are cooled.
17. The process of claim 16 wherein one or both of the further pair of opposed rolls are chilled at a temperature below room temperature.
18. The process of claim 16 wherein before the passing the fabric through the further pair of opposed rolls, spraying an additive onto the surface of the fabric.
19. A process for producing a polyvinyl alcohol fabric having at least one surface that is coalesced and has a reduced porosity which comprises the step of applying heat and pressure to a polyvinyl alcohol fabric by a pair of opposed calendar rollers wherein one of the rollers is a heated metal roller and the other one of the rollers is unheated and includes a surface coating of a high melting polymer film and is relatively softer that the heated metal roller, wherein the polyvinyl fabric has a moisture content of 5 to 15% by weight so as to increase the moisture at the surface and cause surface fibers on a surface of the fabric to coalesce and to lower its surface porosity to a desired level, further comprising after applying heat and pressure, passing the fabric through a further pair of opposed rolls, wherein one or both of the further pair of opposed rolls are cooled.
20. A process for producing a polyvinyl alcohol fabric having at least one surface that is coalesced and has a reduced porosity which comprises the step of applying heat and pressure to a polyvinyl alcohol fabric having a moisture content of at least 5-10% by weight so as to increase the moisture at the surface and cause surface fibers on a surface of the fabric to coalesce and to lower its surface porosity to a desired level, wherein the initial fabric is passed through a pair of calendar rolls, wherein one of the rolls is a heated roller and an opposed one of the rolls is an unheated roller, and wherein the unheated calendar roll is relatively softer than the heated calendar roll.