Microwave shielding effectiveness based on polyvinyl alcohol/silver hybrid nanocomposites
A composite material for electromagnetic interference shielding is provided. The composite material comprises a polymer matrix with metal nanoparticles dispersed within the matrix. Methods of characterizing the nanocomposites are provided and demonstrate commercially relevant mechanical and electrical properties, particularly an electromagnetic interference shielding effectiveness in the microwave frequency. An economical process for preparing the nanocomposites is also provided.
1. A nanocomposite shielding material, comprising;
a polyvinyl alcohol matrix,
silver nanoplatelets dispersed in the matrix,
wherein the nanocomposite shielding material absorbs electromagnetic radiation at a frequency of 1-12GHz, and
wherein the silver nanoplatelets have a thickness of 4-8 nm and an average edge length of 2-8 μm.
2. The nanocomposite shielding material of claim 1 , which comprises from 1-10 weight percent silver nanoplatelets relative to the total weight of the nanocomposite shielding material.
3. The nanocomposite shielding material of claim 2 , wherein the silver nanoplatelets form seamlessly interconnected infinite conductive networks with a separation of no more than 0.01-100 μm.
4. The nanocomposite shielding material of claim 3 , which has a tensile strength of 20-50 MPa, a Young's modulus of 2-30 MPa, a hardness shore A of 30-70 MPa and an elongation at break of 90-5%.
5. The nanocomposite shielding material of claim 3 , which has a conductivity of 10 −14 -10 4 ohm −1 cm −1 and has a percolation threshold of 1.0-2.0 weight percent silver nanoplatelets relative to the total weight of the nanocomposite shielding material.
6. The nanocomposite shielding material of claim 3 , which has a dielectric constant of 1-85.
7. The nanocomposite shielding material of claim 3 , which has an electromagnetic absorption loss of 5-65 dB and an electromagnetic reflection loss of 1-20 dB.
8. The nanocomposite shielding material of claim 3 , which has an electromagnetic shielding effectiveness, which is the sum of the absorption loss and the reflection loss, of 6-85 dB.
9. A process for forming the nanocomposite shielding material of claim 1 , comprising;
dissolving polyvinyl alcohol in deionized water to form a polyvinyl alcohol solution and bubbling nitrogen gas into the polyvinyl alcohol solution, then
adding a solution of a silver salt precursor in distilled water to the polyvinyl alcohol solution and stirring to form a reaction mixture, then
adding a reducing agent to the reaction mixture and stirring, then
ultrasonically irradiating the reaction mixture to form a reduced reaction mixture, then
cooling the reduced reaction mixture and centrifuging with distilled water to obtain a polyvinyl alcohol silver nanocomposite solution, then
casting the polyvinyl alcohol silver nanocomposite solution and drying.
10. The process of claim 9 , wherein the silver salt precursor is AgNO 3 .
11. The process of claim 9 , wherein the reducing agent is β- D -Glucose.
12. An electronic device comprising the nanocomposite shielding material of claim 1 , wherein the nanocomposite shielding material is present in or on said electronic device.