Method for fabricating super mirror finish stainless steel decorative sheet
The present invention provides a method for fabricating a super mirror finish stainless steel sheet uses the following steps: 1) rough machining, wherein a 400-450 grit sandpaper or scouring pad is used to remove an oxide layer on a surface of a stainless steel decorative sheet; 2) finish machining, wherein a 240-1,000 grit graphite grinding wheel is used to perform finish grinding; and 3) polishing processing, wherein an abrasive material is used to perform polishing. For the finish grinding and the polishing that are performed by using the grinding wheel and the abrasive material respectively, a multi-shaft polishing system is used to drive a grinding wheel, and a cylinder is controlled to adjust a force of each polishing shaft, which enables a stainless steel decorative sheet to have a surface finish under 0.01 μm and a reflectivity above 69%.
1. A method for fabricating a super mirror finish stainless steel sheet, comprising the following steps:
1) performing rough machining on a 2B or BA stainless stell sheet, by using a 400-450 grit sandpaper or scouring pad to remove an oxide layer on a surface of the stainless steel sheet;
2) performing finish machining on the stainless steel sheet from step 1), by using a 240-1,000 grit graphite grinding wheel to perform finish grinding;
3) performing polishing processing on the stainless steel sheet from step 2), by using an abrasive material slurry together with polishing wheels, wherein the stainless steel sheet from step 2) is subject to a multi-shaft polishing system, and each polishing shaft drives a polishing wheel, and a cylinder is used to adjust pressure for each polishing shaft in the multi-shaft polishing system, so that all shafts are driven under a same pressure and have equal polishing force
4) obtaining a super mirror finish stainless steel sheet, having a surface finish under 0.01 μm and a reflectivity about 69%.
2. The method according to claim 1 , further comprising transferring the stainless steel sheet in steps 1)-3) between rollers, and using a soft and elastic sponge roller as a top roller.
3. The method according to claim 1 wherein the abrasive material slury is made by the following method steps:
adding 5-8 kg of aluminum oxide into 1,000 kg water, and then adding 20 kg oxydol to the aluminum oxide mixture;
wherein the grain size of the aluminum oxide is selected from 2,000 grits, 4,000 grits, and 6,000 grits.