Water-soluble film, packaging bag, content release body, and method for producing water-soluble film
To provide a water-soluble film having excellent solubility, a packaging bag using the water-soluble film, a content release body using the water-soluble film, and a method for producing a water-soluble film. It is a water-soluble film prepared by film-forming a raw material containing a polyvinyl alcohol-based resin and a bisulfite. A bisulfite is added to the raw material containing the polyvinyl alcohol-based resin. Owing to this, the decrease in solubility of the water-soluble film is suppressed even though the raw material is maintained in a heating state for a predetermined time. This effect is the effect characteristic in a bisulfite, and is the effect that is not obtained in the case where a sulfite is used.
1. A water-soluble film prepared by film-forming a raw material comprising a polyvinyl alcohol-based resin and a bisulfite,
wherein the polyvinyl alcohol-based resin comprises at least one anionic group-modified PVA-based resin selected from the group consisting of a maleic acid-modified PVA-based resin, an itaconic acid-modified PVA-based resin, an acrylic acid-modified PVA-based resin, and a methacrylic acid-modified PVA-based resin.
2. The water-soluble film according to claim 1 ,
wherein the bisulfite is a water solubility deterioration inhibitor.
3. The water-soluble film according to claim 1 , obtained by
maintaining the raw material comprising the polyvinyl alcohol-based resin and the bisulfite in a heating state for a predetermined time, and
film-forming the raw material.
4. The water-soluble film according to claim 1 ,
wherein the raw material further comprises a water-soluble polymer in an amount of 20 parts by mass or less per 100 parts by mass of the PVA-based resin.
5. The water-soluble film according to claim 1 ,
wherein the bisulfite comprises at least one kind selected from the group consisting of sodium bisulfite, potassium bisulfite and ammonium bisulfite.
6. The water-soluble film according to claim 1 ,
wherein when the raw material is maintained at 85° C. and the water-soluble film is formed to have a thickness of 75 μm, R represented by the following formula satisfies 0.001≦R≦1.4:
R =( S 2 −S 1 )÷( T 2 −T 1 )×24
Change rate of dissolution time per 24 hour-heating: R
Heating time: T 1 (h)
Heating time: T 2 (h) (here, T 1 <T 2 )
Dissolution time of film using raw material of heating time T 1 : S 1 (s)
Dissolution time of film using raw material of heating time T 2 : S 2 (s).
7. A packaging bag formed from the water-soluble film described in claim 1 .
8. A content release body comprising a content wrapped with the water-soluble film described in claim 1 , and capable of releasing the content on contact with water.
9. A method for producing a water-soluble film, comprising
maintaining a raw material comprising a polyvinyl alcohol-based resin and a bisulfite in a heating state for a predetermined time, and
film-forming the raw material,
wherein the polyvinyl alcohol-based resin comprises at least one anionic group-modified PVA-based resin selected from the group consisting of a maleic acid-modified PVA-based resin, an itaconic acid-modified PVA-based resin, an acrylic acid-modified PVA-based resin, and a methacrylic acid-modified PVA-based resin.
10. The method for producing a water-soluble film according to claim 9 , wherein the temperature of the heating state is in a range of from 60° C. to 100° C.
11. The method for producing a water-soluble film according to claim 9 , wherein the time period of the predetermined time is in a range of from 1 hour to 360 hours.
12. A water-soluble film comprising a polyvinyl alcohol-based resin and a bisulfite,
wherein the polyvinyl alcohol-based resin comprises at least one anionic group-modified PVA-based resin selected from the group consisting of a maleic acid-modified PVA-based resin, an itaconic acid-modified PVA-based resin, an acrylic acid-modified PVA-based resin, and a methacrylic acid-modified PVA-based resin.
13. The water-soluble film according to claim 12 ,
wherein the bisulfite is a water solubility deterioration inhibitor.
14. The water-soluble film according to claim 12 , obtained by
maintaining the raw material comprising the polyvinyl alcohol-based resin and the bisulfite in a heating state for a predetermined time, and
film-forming the raw material.
15. The water-soluble film according to claim 12 ,
wherein the raw material further comprises a water-soluble polymer in an amount of 20 parts by mass or less per 100 parts by mass of the PVA-based resin.
16. The water-soluble film according to claim 12 ,
wherein the bisulfite comprises at least one kind selected from the group consisting of sodium bisulfite, potassium bisulfite and ammonium bisulfite.
17. The water-soluble film according to claim 12 ,
wherein when the raw material is maintained at 85° C. and the water-soluble film is formed to have a thickness of 75 μm, R represented by the following formula satisfies 0.001≦R≦1.4:
R =( S 2 −S 1 )÷( T 2 −T 1 )×24
Change rate of dissolution time per 24 hour-heating: R
Heating time: T 1 (h)
Heating time: T 2 (h) (here, T 1 <T 2 )
Dissolution time of film using raw material of heating time T 1 : S 1 (s)
Dissolution time of film using raw material of heating time T 2 : S 2 (s).
18. A packaging bag formed from the water-soluble film described in claim 12 .
19. A content release body comprising a content wrapped with the water-soluble film described in claim 12 , and capable of releasing the content on contact with water.