Polishing pad and preparing method thereof
The present disclosure relates to a porous polishing pad including pores by carbon dioxide gas generated by a reaction between a prepolymer and a hydrophilic polymer, and a method of preparing the porous polishing pad.
1. A method of preparing a porous polishing pad, comprising:
dispersing a hydrophilic polymer material in powder form containing absorbed moisture, in an isocyanate-containing prepolymer; and
generating carbon dioxide by a reaction between the isocyanate groups of said prepolymer and the moisture in said hydrophilic polymer material to form pores in the prepolymer, wherein said hydrophilic polymer powder has a moisture content of from about 0.2 wt% to about 10 wt%, wherein the moisture content is achieved by keeping the hydrophilic polymer powder under an atmosphere having a humidity of about 1% to about 50% for about 1 to about 48 hours, and wherein particles of said hydrophilic polymer powder range in size from about 1 μm to about 150 μm.
2. The method of preparing a porous polishing pad of claim 1 , wherein the hydrophilic polymer material is selected from the group consisting of polyvinyl alcohol, polyethylene glycol, polyvinyl acetate, polyacrylic acid, polyethylene oxide, isoprene sulfonate, and mixtures thereof.
3. The method of preparing a porous polishing pad of claim 1 , wherein a curing agent is added during the reaction between the prepolymer and the hydrophilic polymer.
4. The method of preparing a porous polishing pad of claim 3 , wherein the curing agent is selected from the group consisting of 4,4′-methylene-bis(2-chloroaniline); 4,4′-methylene-bis(3-chloro-2,6-diethylaniline); dimethyl thiotoluenediamine; trimethylene glycol di-p-aminobenzoate; polytetramethylene oxide di-p-aminobenzoate; polytetramethylene oxide mono-p-aminobenzoate; polypropylene oxide di-p-aminobenzoate; polypropyleneoxide mono-p-aminobenzoate; 1,2-bis(2-aminophenylthio)ethane; 4,4′-methylene-bis-aniline; diethyltoluenediamine; 5-tert-butyl-2,4-toluenediamine; 3-tert-butyl-2,6-toluenediamine; 5-tert-amyl-2,4- toluenediamine; 3-tert-amyl-2,6-toluenediamine; chlorotoluenediamine; and mixtures thereof.
5. The method of claim 1 , wherein the hydrophilic polymer powder particle size ranges from about 10 μm to about 100 μm.
6. The method of claim 1 , wherein said hydrated hydrophilic polymer is uniformly dispersed in said isocyanate-containing prepolymer.
7. The method of claim 6 , wherein a uniform distribution of pores ranging in size from about 1 μm to about 200 μm is produced by controlling the temperature, stirring speed and stirring time of the process.
8. The method of claim 1 , wherein said moisture content is about 0.4 wt% to about 10 wt%.
9. The method of claim 1 , wherein said moisture content is about 0.6 wt% to about 10 wt%.