Method and apparatus for testing performance of thermal barrier coating layer

1. A method for testing thermal performance of a coating layer, the method comprising:

obtaining a first thermal gradient by exposing one side of a metal base test piece to heat and exposing another side of the metal base test piece to a cooling air;

obtaining a second thermal gradient by exposing a coating layer side of a coating layer test piece to heat and exposing an opposite side to a cooling air, the second thermal gradient being used to calculate a surface temperature of both sides of the metal base test piece;

calculating an exterior temperature T f of a coating layer of the coating layer test piece and a temperature T e of a boundary side of the coating layer using the first thermal gradient; and

testing thermal performance of the coating layer by calculating a temperature difference T Δ between the exterior temperature T f of the coating layer and the temperature T e of the boundary side of the coating layer, wherein a higher value of the calculated temperature difference indicates a higher thermal performance of the coating layer.

2. The method according to claim 1 , further comprising:

in response to obtaining of the first thermal gradient, performing a first surface temperature calculating step of calculating a surface temperature of both sides of the metal base test piece using the obtained first thermal gradient, and performing a convective heat transfer coefficient calculating step of calculating a convective heat transfer coefficient of an interior of a furnace producing the heat and the cooling air using surface temperatures of both sides of the test piece of the metal base, and performing a second surface temperature calculating step of calculating a surface temperature of both sides of the test piece of the metal layer using the obtained second thermal gradient; and

wherein the calculating of the exterior temperature T f comprises calculating the exterior temperature T f of the coating layer and the calculating of the temperature T e of the boundary side of the coating layer comprises using the convective heat transfer coefficient and the surface temperatures of both sides of a metal layer of the coating layer test piece or the metal base test piece.

3. The method according to claim 1 ,

wherein the obtaining of the first thermal gradient comprises measuring an internal temperature at different locations along a thickness direction of the metal base test piece, and

the obtaining of the second thermal gradient comprises measuring an internal temperature at different locations along a thickness direction of a metal layer of the coating layer test piece.

4. The method according to claim 2 ,

wherein the obtaining of the first thermal gradient comprises measuring an internal temperature at different locations along a thickness direction of the metal base test piece, and

the obtaining of the second thermal gradient comprises measuring an internal temperature at different locations along a thickness direction of a metal layer of the coating layer test piece.

5. The method according to claim 2 , wherein the first thermal gradient or the second thermal gradient representing an internal temperature along a thickness direction of the metal base test piece or the coating layer test piece is determined by using the following formula:

T=aX+b,

wherein T represents a temperature along the thickness direction of the metal base test piece or the coating layer test piece;

X represents coordinates along the thickness direction of the metal base test piece or the coating layer test piece; and

a and b each represent a numerical value.

6. The method according to claim 3 ,

wherein the first temperature gradient or the second temperature gradient representing an internal temperature along a thickness direction of the metal base test piece or the coating layer test piece is determined by using the following formula:

T=aX+b,

wherein T represents a temperature along the thickness direction of the metal base test piece or the coating layer test piece;

X represents coordinates along the thickness direction of the metal base test piece or the coating layer test piece; and

a and b each represent a numerical value.

7. The method of claim 1 , wherein the metal base test piece comprises a metal base having a shape of a coin, and the coating layer test piece comprises a second metal base having a shape of a coin and a ceramic coating layer disposed on one surface of the second metal base.

8. A non-transitory computer readable recording medium storing an instruction that causes a computer to perform the method of claim 1 .

9. An apparatus for evaluating thermal performance of a coating layer, the apparatus comprising:

a metal-base test piece comprising a comprising a metal having a shape of a coin a coating layer test piece comprising a second metal base having a ceramic coating layer;

a processor configured to, using a temperature measuring device:

determine a first thermal gradient of the metal-base test piece in response to receiving a temperature measurement taken while one side of the metal-base test piece is exposed to heat and another side of the metal-base test piece is exposed to a cooling air;

determine a second thermal gradient of a coating-layer test piece in response to receiving a temperature measurement taken while the coating layer side of the coating-layer test piece is exposed to heat and an opposite side of the coating layer test piece is exposed to a cooling air, the second thermal gradient used to calculate a surface temperature of both side of the metal base test piece;

calculate an exterior temperature T f of a coating layer in the coating layer test piece and a temperature T e of a boundary side of the coating layer using the first thermal gradient; and

evaluate the thermal performance of the coating layer based on a temperature difference between the exterior temperature T f of the coating layer and the temperature T e of the boundary side of the coating layer, wherein a higher value of the calculated temperature difference indicates a higher thermal performance of the coating layer.

10. The apparatus of claim 9 , wherein the temperature measuring device is inserted into a first hole and a second hole of the metal base test piece and the coating layer test piece and configured to measure a temperature on surfaces of the metal base test piece and the coating layer test piece.