Addition-curable liquid silicone rubber composition
Provided is an addition-curable liquid silicone rubber composition which is suppressed in thickening over time even in cases where a silicone raw rubber is added into a liquid silicone rubber composition, thereby having excellent storage stability, and which provides a silicone rubber that has a low hardness after being cured. An addition-curable liquid silicone rubber composition which contains: (A) an alkenyl group-containing organopolysiloxane having an average polymerization degree of 1,500 or less, which is in a liquid state at room temperature; (B) an organopolysiloxane having an average polymerization degree of 2,000 or more, which is in the form of a raw rubber at room temperature; (C) an organohydrogen polysiloxane; (D) a fumed silica having a BET specific surface area of 130 m 2 /g or more; (E) an organosilane and/or organopolysiloxane having a silanol group; and (F) an addition reaction catalyst. This addition-curable liquid silicone rubber composition provides a low-hardness silicone rubber which has a hardness (durometer A) of 5-40 after being cured.
1. An addition-curable liquid silicone rubber composition which gives a low-hardness silicone rubber having a durometer A hardness after curing of from 5 to 40, comprising:
(A) 100 parts by weight of an alkenyl group-containing organopolysiloxane that includes at least two silicon-bonded alkenyl groups per molecule, has an average degree of polymerization of not more than 1,500 and is liquid at room temperature;
(B) 1 to 200 parts by weight of an organopolysiloxane that has an average degree of polymerization of at least 2,000 and is raw rubber-like at room temperature;
(C) an organohydrogenpolysiloxane containing at least two silicon-bonded hydrogen atoms per molecule, in an amount of 0.2 to 20 parts by weight per 100 parts by weight of components (A) and (B) combined;
(D) fumed silica having a BET specific surface area of at least 130 m 2 /g, in an amount of 5 to 50 parts by weight per 100 parts by weight of components (A) to (C) combined;
(E) trimethylsilanol or a linear organopolysiloxane which is liquid at room temperature, has an average degree of polymerization of 5 to 80, and has a silanol group at one end or at both ends of the molecular chain, in an amount of 0.1 to 10 parts by weight per 100 parts by weight of components (A) to (D) combined; and
(F) a catalytic amount of an addition reaction catalyst.
2. The addition-curable liquid silicone rubber composition of claim 1 , wherein component (D) is hydrophobically treated fumed silica.
3. The addition-curable liquid silicone rubber composition of claim 1 , further comprising:
(G) a silica surface treatment agent, in an amount of 0.1 to 50 parts by weight per 100 parts by weight of component (D).
4. The addition-curable liquid silicone rubber composition according to claim 1 , wherein the silicone rubber mixture of components (A), (B) and (D) to (F) or the silicone rubber mixture of components (A) to (E) has a viscosity at 25° C. and a shear rate of 1 s −1 when stored at 70° C. for 7 days which is not more than two times the viscosity at 25° C. and a shear rate of 1 s −1 immediately following production.