Hard metal composition
A process for producing a component includes providing a composition comprising hard material particles and a binder metal, and sintering the composition at a sintering temperature of from 1250° C. to 1400° C. for a period of from 3 to 15 minutes. The hard material particles comprise an inner core comprising fused tungsten carbide and an outer shell comprising tungsten carbide. The binder metal is selected from the group consisting of Co, Ni, Fe and alloys comprising at least one metal selected from Co, Ni and Fe.
1. A process for producing a component, the process comprising:
providing a composition comprising:
hard material particles comprising an inner core comprising fused tungsten carbide and an outer shell comprising tungsten carbide, and
a binder metal selected from the group consisting of Co, Ni, Fe; and
sintering the composition at a sintering temperature of from 1250° C. to 1400° C. for a period of from 3 to 15 minutes,
wherein, the sintering is carried out at a gas pressure of less than 10 −3 bar.
2. The process as recited in claim 1 , wherein the hard material particles further comprise a content of bound carbon of from 4 to 6 wt %, based on the total hard material particles.
3. The process as recited in claim 1 , wherein a thickness of the outer shell is about 0.05 to 0.4 times an average particle size of the hard material particles.
4. The process as recited in claim 1 , wherein
the inner core comprises at least one of the fused tungsten carbide and an alloy comprising the fused tungsten carbide and at least one further carbide of the elements selected from groups 4B, 5B and 6B of the Periodic Table of the Elements, and
the outer shell comprises an alloy comprising the tungsten carbide and at least one further carbide of the elements selected from groups 4B, 5B and 6B of the Periodic Table of the Elements.
5. The process as recited in claim 1 , wherein the sintering is carried out at a sintering temperature of from 1300° C. to 1370° C.
6. The process as recited in claim 1 , wherein the sintering is carried out for a period of from 3 to 10 minutes.
7. The process as recited in claim 1 , wherein the sintering is a liquid-phase sintering.
8. The process as recited in claim 1 , wherein the sintering is carried out by heating at a heating rate of above 50 K/min until the sintering temperature is attained.
9. The process as recited in claim 1 , further comprising cooling the composition from the sintering temperature to 500° C., wherein the cooling is carried out at a cooling rate of below 100 K/min.
10. The process as recited in claim 1 , wherein the composition comprises from 60 to 95 wt % of the hard material particles and from 5 to 40 wt % of the binder metal, in each case based on a total weight of the composition.
11. The process as recited in claim 1 , wherein the sintering is carried out while applying a pressure of from 20 to 80 MPa to the composition.
12. A process for producing a component, the process consisting of:
providing a composition consisting of:
hard material particles consisting of an inner core comprising fused tungsten carbide and an outer shell comprising tungsten carbide, and
a binder metal selected from the group consisting of Co, Ni, Fe;
sintering the composition at a sintering temperature of from 1250° C. to 1400° C. for a period of from 3 to 15 minutes; and
cooling the composition from the sintering temperature to 500° C., wherein the cooling is carried out at a cooling rate of from 30 to 70 K/min.