Process for solid-state cultivation of mycelium on a lignocellulose substrate
In one embodiment, the process combines a fraction (up to 15%) of a lignocellulose substrate with supplemental nutritional material and hydrates the fraction to a moisture content of from 40% to 70% by weight. The hydrated substrate fraction is heat processed to remove ambient bioburden (yeast, mold, bacteria) and to maintain the hydrated substrate fraction in an aseptic condition. Thereafter, the hydrated substrate fraction is inoculated with a fungus and incubated to obtain a myceliated substrate which is then reduced into discrete particles. The remaining fraction of the substrate is combined with water and then combined with the discrete particles of myceliated substrate and incubated to obtain a second myceliated substrate which is then reduced into discrete particles. The second myceliated substrate is combined with supplemental nutritional material and incubated to obtain a third myceliated substrate composed of at least 10% mycelium.
1. A process for solid-state cultivation of mycelium on a lignocellulose substrate comprising the steps of
obtaining a lignocellulose substrate;
combining a first fraction of said substrate with supplemental nutritional material at a ratio of up to 14% of the dry mass of said fraction and hydrating said fraction to a moisture content of from 40% to 70% by weight;
heat processing the hydrated substrate fraction for a period of time sufficient to eliminate ambient bioburden and to maintain the hydrated substrate fraction in an aseptic condition;
thereafter inoculating the hydrated substrate fraction with a predetermined fungus;
thereafter incubating the inoculated substrate for a period of time to allow said fungus to grow hyphae and to allow said hyphae to form a network of interconnected mycelia cells through and around discrete particles of said substrate fraction to obtain a myceliated substrate;
thereafter reducing the myceliated substrate into discrete particles;
combining the remaining fraction of said substrate with water to obtain a moisture content of 40% to 70%;
thereafter combining the moistened remaining fraction of said substrate with said discrete particles of myceliated substrate into a mass and incubating said mass for a period of time to allow said fungus in said discrete particles of myceliated substrate to grow hyphae and to allow said hyphae to form a network of interconnected mycelia cells through and around discrete particles of said remaining fraction of said substrate to obtain a second myceliated substrate;
thereafter reducing the second myceliated substrate into discrete particles; and
combining the discrete particles of said second myceliated substrate with supplemental nutritional material at a ratio of up to 14% of the dry mass of said second myceliated substrate and incubating said discrete particles and said nutritional material for a period of time to allow said fungus in said discrete particles of myceliated substrate to grow hyphae and to allow said hyphae to form a network of interconnected mycelia cells through and around discrete particles of said remaining fraction of said substrate to obtain a third myceliated substrate composed of at least 10% mycelium.
2. A process as set forth in claim 1 wherein said first fraction is up to 15% of said substrate.
3. A process as set forth in claim 1 wherein said lignocellulose substrate is comprised entirely of gymnosperm wood.
4. A process as set forth in claim 1 wherein said lignocellulose substrate is between 50% and 100% gymnosperm wood blended with other plant matter.
5. A process as set forth in claim 4 wherein the gymnosperm fraction is comprised of at least one wood species.
6. A process as set forth in claim 1 wherein said lignocellulose substrate has a native resin and monoterpene content.
7. A process as set forth in claim 6 has an additional terpene supplement.
8. A process as set forth in claim 1 wherein said lignocellulose substrate is a plant matter not derived from a gymnosperm tree species and is supplemented with terpene.
9. A process as set forth in claim 1 further comprising the step of compressing said third myceliated substrate to a density of greater than 20 pounds per cubic foot.
10. A process as set forth in claim 1 wherein said fungus is a soft rot species and said step of incubating said discrete particles of said second myceliated substrate and said nutritional material is conducted for a period of time to allow said fungus to reduce hemicellulose by up to 30% and simple sugars by up to at least 70%.
11. A process as set forth in claim 1 wherein said fungus is a white rot species and said step of incubating said discrete particles of said second myceliated substrate and said nutritional material is conducted for a period of time to allow said fungus to reduce cellulose by up to at least 10% and lignin by up to at least 25%.
12. A process as set forth in claim 1 wherein said fungus is one of a saprophytic white rot, brown rot, or soft rot and is characterized in being tolerant of the monoterpene content associated with said substrate and in producing structural cellular components comprised of thick-walled cells.
13. A process as set forth in claim 12 wherein said substrate contains up to 25% resin (w:w).
14. A process as set forth in claim 1 further comprising the steps of
reducing the third myceliated substrate into discrete particles; and
combining the discrete particles of said third myceliated substrate with supplemental nutritional material at a ratio of up to 14% of the dry mass of said third myceliated substrate and incubating said discrete particles and said nutritional material for a period of time sufficient for the total dry mass of said third myceliated substrate to be composed of at least 10% fungal biomass.