Integrated process for the production of clinker with treatment of bypass dusts produced by the kiln
It is described an integrated process for the production of clinker by dry process, with treatment in continuous of by-pass dusts produced by the kiln, wherein the solid matter to treat consists of bypass dusts of a clinker production process, containing compounds of chloride, sodium, potassium and sulphur, such a process comprising the following steps: a) extraction of the bypass dusts directly from the phase of quench, without intermediate storage, at a temperature comprised between 150 and 200° C., with a moisture content varying from 0.1 to 3% by weight, preferably from 0.1 to 0.5% by weight, and with a quantity of calcium carbonate lower than 55% by weight; b) mixing of said dusts coming from step a), within a maximum time comprised between 2 and 10 minutes, preferably lower than about 5 minutes, with water up to a water/dusts ratio varying from 2:1 to 4:1, preferably from 2.5:1 to 3.5:1, in a way to obtain a mixture with a moisture content comprised between 45 and 75% by weight, preferably between 50% and 55% by weight, even more preferably equal to about 50% by weight; c) mechanical stirring of the mixture diluted up to complete dissolution of the soluble salts; d) mechanical separation of the mixture so diluted in a liquid fraction containing water and soluble salts and in a solid fraction in form of cake or crust.
1. An integrated process for the production of clinker by dry process, with treatment in continuous of bypass dusts produced by the kiln, wherein the solid matter to treat consists of bypass dusts of a clinker production process, containing compounds of chloride, sodium, potassium and sulphur, such a process comprising the following steps:
a) extraction of the bypass dusts directly from the phase of quench, without intermediate storage, at a temperature comprised between 150 and 200° C., with a moisture content varying from 0.1 to 3% by weight, and with a quantity of calcium carbonate lower than 55% by weight;
b) mixing of said dusts coming from phase a), within a maximum time comprised between 2 and 10 minutes, with water up to a water/dusts ratio varying from 2:1 to 4:1, in a way to obtain a mixture with a moisture content comprised between 45 and 75% by weight;
c) mechanical stirring of the mixture diluted up to complete dissolution of the soluble salts; and
d) mechanical separation of the mixture so diluted in a liquid fraction containing water and soluble salts and in a solid fraction in form of cake or crust.
2. The integrated process according to claim 1 , wherein the sum of steps a)-b) is carried out in a period of time varying from 2 to 10 minutes.
3. The integrated process according to claim 1 , wherein the reintroduction of the treated solid fraction is provided upstream of the grinding of the raw mixture.
4. The integrated process according to claim 2 , wherein the reintroduction of the treated solid fraction is provided upstream of the grinding of the raw mixture.
5. The integrated process according to claim 1 , wherein the sum of steps a)-b) is carried out in a period of time lower than about 5 minutes.
6. The integrated process according to claim 1 , wherein the moisture content of step a) varies from 0.1 to 0.5% by weight.
7. The integrated process according to claim 1 , wherein the water/dusts ratio of step b) varies from 2.5:1 to 3.5:1.
8. The integrated process according to claim 1 , wherein the moisture content of step b) varies between 50% and 55% by weight.