Oxygen reduction reaction electrocatalyst
The oxygen reduction reaction electrocatalyst is a Pt/N/C electrocatalyst that provides an efficient ORR catalyst suitable for use in polymer electrolyte membrane (PEM) fuel cells, for example. The oxygen reduction reaction electrocatalyst is in the form of platinum nanoparticles embedded in a nitrogen-enriched mesoporous carbon matrix, particularly a nitrogen-enriched graphite matrix. The nitrogen-enriched graphite matrix has an average surface area of 240.4 m 2 /g, and the platinum nanoparticles each have an average diameter between 10 nm and 12 nm.
1. An oxygen reduction reaction electrocatalyst, comprising platinum nanoparticles embedded in a nitrogen-enriched mesoporous graphite matrix having an average surface area of 240.4 m2/g.
2. The oxygen reduction reaction electrocatalyst as recited in claim 1 , wherein the platinum nanoparticles each have an average diameter between 10 nm and 12 nm.
3. A method of making an oxygen reduction reaction electrocatalyst, comprising the steps of:
reacting 2,4,6-trihydrazinyl-1,3,5-triazine with p-terephthaldehyde in an organic solvent to form a polymeric solution;
refluxing the polymeric solution to produce a conductive polymer having the structure:
adding the conductive polymer to methanol to form a polymeric suspension;
adding H2PtCl4 to the polymeric suspension to form a mixture;
stirring and sonicating the mixture;
drying the stirred and sonicated mixture to yield platinum nanoparticles suspended in the conductive polymer; and
annealing the suspension of platinum nanoparticles in the conductive polymer to yield platinum nanoparticles embedded in a mesoporous, graphitic carbon matrix forming the oxygen reduction reaction electrocatalyst.
4. The method of making an oxygen reduction reaction electrocatalyst as recited in claim 3 , further comprising the step of reacting hydrazine hydrate with cyanuric chloride in a polar organic solvent to form the 2,4,6-trihydrazinyl-1,3,5-triazine.
5. The method of making an oxygen reduction reaction electrocatalyst as recited in claim 3 , wherein the step of refluxing the polymeric solution comprises refluxing the polymeric solution for 30 hours.
6. The method of making an oxygen reduction reaction electrocatalyst as recited in claim 5 , wherein the step of stirring and sonicating the mixture comprises stirring the mixture for one hour at room temperature.
7. The method of making an oxygen reduction reaction electrocatalyst as recited in claim 6 , wherein the step of stirring and sonicating the mixture further comprises sonicating the mixture at a temperature of 40° C. for four hours.
8. The method of making an oxygen reduction reaction electrocatalyst as recited in claim 7 , wherein the annealing step comprises annealing the suspension of platinum nanoparticles in the conductive polymer in a tube furnace at a temperature of 800° C. at a heating rate of 5° C./min.