Urethane-crosslinked biodegradable elastomers
Among other things, the present disclosure provides compositions and methods for an elastomeric cross-linked polyester material. Such an elastomeric cross-linked polyester material, in some embodiments, comprises a plurality of polymeric units of the general formula (-A-B—) p , wherein p is an integer greater than 1; and a plurality of urethane cross-links each of which covalently links two polymeric units to one another, which two linked polymeric unit each had at least one free hydroxyl or amino group prior to formation of the crosslink.
1. A composition comprising:
a polyester material, the material comprising a plurality of A and B components, wherein the A and B components form a plurality of polymeric backbones formed of (-A-B—) repeat units, having a general formula (-A-B—) p , wherein:
p is an integer greater than 1;
the (-A-B—) repeat units have a chemical structure achieved when a polyol component A′ is condensed with a polyacid component B′;
at least two of the (-A-B—) repeat units within each of the polymeric backbones have at least one free hydroxyl group present thereon on the A component of the at least two (-A-B—) repeat units within the polymeric backbones;
wherein the polyester material has a molecular weight of between about 3,000 and about 50,000 Daltons; and
a polyisocyanate crosslinker;
wherein the at least one free hydroxyl group to the polyisocyanate crosslinker is present at a molar ratio of between 1:0.3 and 1:0.8;
wherein the polyester material crosslinked by the polyisocyanate crosslinker is an elastomeric polyester material cross-linked by a plurality of urethane crosslinks which covalently link the polymeric backbones at the A components of the at least two (-A-B—) repeat units; and
wherein the elastomeric polyester material crosslinked by the plurality of urethane crosslinks has one or more properties selected from the group consisting of:
the elastomeric polyester material as a non-porous film with the thickness of 200 μm transmits more than 75% of incident light;
the elastomeric polyester material has a Young's modulus of between about 0.5 MPa and about 30 MPa;
the elastomeric polyester material has a tensile strength of between about 0.5 MPa and about 15 MPa;
the elastomeric polyester material elongation of between about 50% and about 600%;
the elastomeric polyester material has a size deformation of below about 20% of its initial length, after tensile loading;
the elastomeric polyester material has tensile strength stable within about 5% to about 30% of the initial strength over 100 cycles of extension;
the elastomeric polyester material has a size deformation stable within about 5% to about 30% of the initial length over 100 cycles of extension; and
combinations thereof.
2. The composition of claim 1 , wherein the polyester material is non-linear.
3. The composition of claim 1 , wherein the polyester material has a molecular weight between about 3,000 and about 25,000 Daltons.
4. The composition of claim 1 , further comprising a catalyst.
5. The composition of claim 1 , further comprising a solvent.
6. The composition of claim 1 , further comprising a porogen.
7. The composition of claim 1 , wherein the polyester material has a molecular weight between about 3,000 and about 20,000 Daltons.
8. An elastomeric cross-linked polyester material comprising:
a plurality of A and B components, wherein the A and B components form a plurality of polymeric backbones formed of (-A-B—) repeat units, having the general formula (-A-B—) p , wherein:
p is an integer greater than 1;
the (-A-B—) repeat units have a chemical structure produced by condensation of a polyol component A′ with a polyacid component B′;
wherein the A component of at least two of the (-A-B—) repeat units within each of the polymeric backbones has at least one free hydroxyl group present thereon, prior to crosslinking;
wherein crosslinking is carried out by a polyisocyanate crosslinker and the at least one free hydroxyl group to the polyisocyanate crosslinker at a molar ratio of between 1:03 and 1:0.8;
wherein urethane cross-links covalently crosslink the polymeric backbones between the A components of the at least two (-A-B—) repeat units within each of the polymeric backbones;
wherein the elastomeric cross-linked polyester material is a non-porous film having a thickness of 200 μm which transmits more than 75% of incident light; and
wherein the elastomeric cross-linked polyester material has one or more properties selected from the group consisting of:
a Young's modulus of between about 0.5 MPa and about 30 MPa;
a tensile strength of between about 0.5 MPa and about 15 MPa;
an elongation of between about 50% and about 600%;
a size deformation of below about 20% of its initial length, after tensile loading;
a tensile strength stable within about 5% to about 30% of the initial strength over 100 cycles of extension;
a size deformation stable within about 5% to about 30% of the initial length over 100 cycles of extension; and
combinations thereof.
9. The elastomeric cross-linked polyester material of claim 8 , wherein the elastomeric cross-linked polyester material as the non-porous film with the thickness of 200 μm transmits more than 80% of incident light.
10. The elastomeric cross-linked polyester material of claim 8 in the form of a patch.
11. A method of making the elastomeric cross-linked polyester material of claim 8 comprising:
providing a polyester material, the material comprising a plurality of A and B components, wherein the A and B components form a plurality of polymeric backbones formed of (-A-B—) repeat units having the general formula (-A-B—) p , wherein:
p is an integer greater than 1;
the (-A-B—) repeat units have a chemical structure formed when a polyol component A′ is condensed with a polyacid component B′;
at least two of the (-A-B—) repeat units within each of the polymeric backbones have at least one free hydroxyl group present thereon on the A component of the at least two (-A-B—) repeat units within the polymeric backbones;
wherein the polyester material has a molecular weight between about 3,000 and about 50,000 Daltons; and
mixing the polyester material with a polyisocyanate crosslinker,
wherein the at least one free hydroxyl group to the polyisocyanate crosslinker is at a molar ratio of between 1:0.3 and 1:0.8, such that the elastomeric urethane cross-linked polyester material comprising a plurality of urethane crosslinks is produced,
wherein the urethane crosslinks covalently crosslink the polymeric backbones between the A components of the at least two (-A-B—) repeat units within each of the polymeric backbones.
12. The method of claim 11 , wherein the step of mixing is conducted in the presence of at least one solvent.
13. The method of claim 12 , wherein the step of mixing is conducted at a temperature less than 45° C.
14. The method of claim 11 , wherein the step of mixing is conducted in the absence of any solvent.
15. The method of claim 14 , wherein the step of mixing is conducted at room temperature.
16. The method of claim 14 , comprising mixing the polyester material with the polyisocyanate crosslinker, and implanting the mixture in an individual.
17. The method of claim 11 , wherein the polyester material has a molecular weight between about 3,000 and about 25,000 Daltons.
18. The method of claim 11 , further comprising a step of providing a catalyst.
19. The method of claim 11 , wherein all steps are performed within 12 hours, 24 hours, or 48 hours.
20. The method of claim 11 , wherein the polyester material has a molecular weight between about 3,000 and about 20,000 Daltons.