Thermally insulating aerogel based rendering materials
In order to produce a high performance thermally insulating rendering, a dry blend is provided that consists essentially of: —60 to 90 Vol.-% of a hydrophobized granular silica aerogel; —0.5 to 30 Vol.-% of a purely mineral binder; —0.2 to 20 Vol.-% of an open-porous water-insoluble or slowly water soluble additive having an accessible pore volume from 10 to 90 Vol.-%; —up to 5 Vol.-% reinforcing fibers; and—up to 5 Vol.-% of processing additives. After mixing the dry blend with water, the slurry thus formed can be applied to a surface or shaped to a self-supporting body using an overpressure without adversely affecting the thermal insulation properties.
1. A dry blend for producing a thermally insulating rendering, consisting essentially of:
60 to 90 Vol.-% of a hydrophobized granular silica aerogel;
0.5 to 30 Vol.-% of a purely mineral binder;
0.2 to 20 Vol.-% of an open-porous water-insoluble or slowly water soluble additive having an accessible pore volume from 10 to 90 Vol.-%;
up to 5 Vol.-% reinforcing fibers;
up to 5 Vol.-% of processing additive; and,
wherein said open-porous additive is pumice.
2. A dry blend for producing a thermally insulating rendering, consisting essentially of:
60 to 90 Vol.-% of a hydrophobized granular silica aerogel;
0.5 to 30 Vol.-% of a purely mineral binder;
0.2 to 20 Vol.-% of an open-porous water-insoluble or slowly water soluble additive having an accessible pore volume from 10 to 90 Vol.-%;
up to 5 Vol.-% reinforcing fibers;
up to 5 Vol.-% of processing additive;
wherein said open-porous additive has a particle size from 0.04 to 4 mm; and,
wherein said open-porous additive is pumice.
3. A dry blend for producing a thermally insulating rendering, consisting essentially of:
60 to 90 Vol.-% of a hydrophobized granular silica aerogel;
0.5 to 30 Vol.-% of a purely mineral binder;
0.2 to 20 Vol.-% of an open-porous water-insoluble or slowly water soluble additive having an accessible pore volume from 10 to 90 Vol.-%;
up to 5 Vol.-% reinforcing fibers;
up to 5 Vol.-% of processing additive;
wherein said open-porous additive has an accessible pore volume from 45 to 55 Vol.-%; and,
wherein said open-porous additive is pumice.
4. The dry blend according to claim 1 , wherein said open-porous additive has a relative water absorption capacity by weight ranging from 1.1 to 2.5.