Polyurea perimeter seal for an aircraft antenna or other aircraft part
A sealant is provided for use on an aircraft or other vehicle. The sealant may be used with a gasket. The sealant is a perimeter seal that comprises a polyurea member. The polyurea member is a self-curing, two-component mix. It may cure to a hardness in the range of about 40 to 100 (Shore A). It may maintain an adequate peel strength to withstand multiple thermal and pressure cycling, and may have a working life, wherein it may be shaped, of less than about eleven minutes.
1. An assembly for use in applying a seal to a junction at an outer perimeter of a first part and a second part, the assembly comprising:
an applicator having a forcing element, a first compartment, a second compartment, and a mixing nozzle in fluid communication with the two compartments;
wherein the first compartment includes a first liquid component and the second compartment a second liquid component, the two components for mixing in the mixing nozzle and curing at the junction, to form a polyurea seal with a hardness in the range of about 40 to 100 (Shore A); and
wherein the linear polyurea member is flame retardant.
2. The assembly of claim 1 , wherein the first liquid component and/or the second liquid component includes carbon black for inhibiting the breakdown of the polyurea seal from ultraviolet radiation.
3. The assembly of claim 1 , wherein the working life of the two component mix measured from the time of mixing is less than about 11 minutes at temperature between about 15° C. and 40° C.
4. The assembly of claim 1 , wherein each of the two components before mixing, have a viscosity of between about 28,000 and 98,000 cps.
5. The assembly of claim 1 , wherein the two components are mixed in a ratio of 1:1 by volume.
6. The assembly of claim 1 , wherein the polyurea seal has a hardener between about 40 to about 90 shore A.
7. An assembly for use in applying a seal to a junction at an outer perimeter of a first part and a second part, the assembly comprising:
an applicator having a forcing element, a first compartment, a second compartment, and a mixing nozzle in fluid communication with the two compartments;
wherein the first compartment includes a first liquid component and the second compartment a second liquid component, the two components for mixing in the mixing nozzle and curing at the junction, to form a polyurea seal with a hardness in the range of about 40 to 100 (Shore A);
wherein the linear polyurea member is flame retardant;
wherein the first liquid component and/or the second liquid component includes carbon black for inhibiting the breakdown of the polyurea seal from ultraviolet radiation; and
wherein the working life of the two component mix measured from the time of mixing is less than about 11 minutes at temperature between about 15° C. and 40° C.
8. The assembly of claim 7 , wherein each of the two components before mixing, have a viscosity of between about 28,000 and 98,000 cps.
9. The assembly of claim 7 , wherein the two components are mixed in a ratio of 1:1 by volume.
10. The assembly of claim 7 , wherein the polyurea seal has a hardener between about 40 to about 90 shore A.
11. An assembly for use in applying a seal to a junction at an outer perimeter of a first part and a second part, the assembly comprising:
an applicator having a forcing element, a first compartment, a second compartment, and a mixing nozzle in fluid communication with the two compartments;
wherein the first compartment includes a first liquid component and the second compartment a second liquid component, the two components for mixing in the mixing nozzle and curing at the junction, to form a polyurea seal with a hardness in the range of about 40 to 100 (Shore A);
wherein the linear polyurea member is flame retardant; and
wherein each of the two components before mixing, have a viscosity of between about 28,000 and 98,000 cps.
12. The assembly in claim 11 , wherein the first liquid component and/or the second liquid component includes carbon black for inhibiting the breakdown of the polyurea seal from ultraviolet radiation.
13. The assembly in claim 11 , wherein the working life of the two component mix measured from the time of mixing is less than about 11 minutes at temperature between about 15° C. and 40° C.
14. The assembly in claim 11 , wherein the two components are mixed in a ratio of 1:1 by volume.
15. The assembly in claim 11 , wherein the polyurea seal has a hardener between about 40 to about 90 shore A.