Hybrid coated cosmetic powders and methods of making and using same
A hybrid coating material and process for pigments and other powders, for example cosmetic powders employs an organometallate, for example a titanate, and a functionalized silicon compound, for example a trialkoxysilane or a functionalized polysiloxane, which covalently bond to each other and to the substrate powder. The coated powders can exhibit excellent hydrophobicity coupled with lipophilicity. Employment of fluorinated silicon compounds may provide hydrophobicity and lipophobicity. Examples show good dispersibility of coated pigments in aqueous, oil and silicone fluids.
1. A coating process for making a hydrophobic coated cosmetic powder, wherein the coating process comprises:
selecting a cosmetic powder having a mean particle size of 0.01 to 20.0 μm, to be hydrophobized with a hybrid coating comprising an organotitanate coating agent and a functionalized silicone coating agent;
dissolving the organotitanate coating agent and the functionalized silicone coating agent in a volatile solvent to produce a solution of the organotitanate coating agent and the functionalized silicone coating agent;
mixing the solution of the organotitanate coating agent and the functionalized silicone coating agent into or spraying the solution of the organotitanate coating agent and the functionalized silicone coating agent on the cosmetic powder to produce a silicone and organotitanate treated cosmetic powder; and
heating the silicone and organotitanate treated cosmetic powder at an elevated temperature, in a range from 60° C. to about 130° C.; and
allowing the silicone and organotitanate treated cosmetic powder to dry, resulting in substantial removal of the solvent,
whereby the organotitanate coating agent and the functionalized silicone coating agent form a hybrid coating which is covalently bonded to the cosmetic powder, and wherein said hybrid coating is applied in an amount resulting in the coating comprising 1.0 to 10.0 percent by weight of the hybrid-coated cosmetic powder.
2. The coating process of claim 1 , wherein the cosmetic powder is hydrophobized with the hybrid coating and hammer milled.
3. The coating process of claim 1 , wherein the cosmetic powder is hydrophobized with the hybrid coating and jet milled.
4. The coating process of claim 1 , wherein the organotitanate and functionalized silicone coating agents are dissolved in isopar C.
5. The coating process of claim 4 , wherein the organotitanate coating agent is a liquid monoalkoxy (C 1 to C 20 ) isostearoyl titanate and the functionalized silicone coating agent is selected from the group consisting of any suitable functionalized silane, functionalized polysiloxane, and functionalized silicon.
6. The coating process of claim 5 , wherein the liquid monoalkoxy (C 1 to C 20 ) isostearoyl titanate coating agent is isopropyl triisostearoyl titanate.
7. The coating process of claim 6 , wherein the cosmetic powder is an ultrafine titanium dioxide, the organotitanate coating agent is isopropyl triisostearoyl titanate and the functionalized polysiloxane coating agent contains reactive Si—H bonds.
8. The coating process of claim 7 , wherein the cosmetic powder is an ultrafine titanium dioxide of an average particle size less than 100 nm, wherein said hybrid coating is contained at an amount of 4.0 percent by weight to the hybrid-coated ultrafine titanium dioxide.
9. The coating process of claim 6 , wherein the cosmetic powder is zinc oxide, the organotitanate coating agent is isopropyl triisostearoyl titanate and the functionalized polysiloxane coating agent contains reactive Si—H bonds.
10. The coating process of claim 9 , wherein the cosmetic powder is zinc oxide of an average particle size less than 100 nm, and wherein said hybrid coating is contained at an amount of 4.0 percent by weight to the hybrid-coated zinc oxide.
11. The coating process of claim 6 , wherein the functionalized silane coating agent is triethoxy octylsilane.
12. The coating process of claim 6 , wherein the functionalized polysiloxane is methyl hydrogen polysiloxane or dimethylpolysiloxane copolymer.
13. The coating process of claim 6 , wherein the functionalized polysiloxane coating agent is a branched silicone.
14. The coating process of claim 13 , wherein the branched silicone is triethoxysilylethylpolydimethylsiloxyethyl dimethicone.
15. The coating process of claim 4 , further comprising:
dispersing the hybrid-coated cosmetic powder in a cosmetic pigment emulsifier using a mixer to create a dispersion; and
grinding the dispersion in a mill.
16. A method as in claim 15 , wherein the volatile solvent liquid is removed from the hybrid-coated cosmetic powder.
17. The coating process of claim 1 , wherein said hybrid coating comprises about 1.0 to about 5.0 percent by weight of the hybrid-coated cosmetic powder.
18. The coating process of claim 17 , wherein said hybrid coating comprises about two percent by weight of the hybrid-coated cosmetic powder.
19. The coating process of claim 1 , wherein the cosmetic powder is selected from the group consisting of titanium dioxide, zinc oxide, and iron oxides.
20. The coating process of claim 1 , wherein the cosmetic powder is an organic coloring pigment.
21. A process as in claim 1 , wherein said mixing or spraying of the solution of the organotitanate coating agent and the functionalized silicone coating agent on the cosmetic powder is done under agitation to produce the treated cosmetic powder.
22. The process of claim 1 wherein the coating agents are dissolved in a volatile solvent or solvents and mixed with or sprayed on the cosmetic powder separately.
23. A coating process for coating a hydrophobic cosmetic powder, comprising:
selecting a cosmetic powder having a mean particle size of 0.01 to 20.0 μm to be hydrophobized with a hybrid coating comprising an organotitanate coating agent and a functionalized silicone coating agent;
dissolving the organotitanate coating agent in a volatile solvent to produce a titanate solution of the organotitanate coating agent;
dissolving the functionalized silicone coating agent in a volatile solvent to produce a solution of the functionalized silicone coating agent;
mixing the silicone solution with the cosmetic powder or spraying the silicone solution onto the cosmetic powder;
mixing the titanate solution with or spraying the titanate solution onto the cosmetic powder, after mixing the silicone solution with the cosmetic powder or spraying the silicone solution onto the cosmetic powder, to produce a silicone and organotitanate treated cosmetic powder; and
heating the silicone and organotitanate treated cosmetic powder at an elevated temperature, in a range from 60° C. to about 130° C.; and
allowing the silicone and organotitanate treated cosmetic powder to dry resulting in substantial removal of the solvent,
whereby the organotitanate coating agent and the functionalized silicone coating agent form a hybrid coating which is covalently bonded to the cosmetic powder, and wherein said coating solution is applied in an amount sufficient to result in said hybrid coating comprising 1.0 to 10.0 percent by weight of the hydrophobized cosmetic powder.
24. A method as in claim 23 , wherein the volatile solvent liquid is removed from the silicone and organotitanate treated cosmetic powder.
25. A method as in claim 23 , wherein mixing the titanate-silicone solution with or spraying the titanate-silicone solution onto the cosmetic powder results in the creation of a pigment mixture, and further comprising removing the liquid component from the pigment mixture to produce a silicone and organotitanate treated cosmetic powder.
26. A method as in claim 23 , wherein the cosmetic powder is selected from the group consisting of titanium dioxide, red iron oxide, yellow iron oxide, black iron oxide, barium lake, mica and silica.
27. A coating process for making a hydrophobic cosmetic powder, wherein the coating process comprises:
selecting a cosmetic powder, from the group consisting of titanium dioxide, red iron oxide, yellow iron oxide, black iron oxide, barium lake, mica and silica with a mean particle size of 0.01 to 20.0 μm, to be hydrophobized with a hybrid coating comprising an organotitanate coating agent and a functionalized silicone coating agent, said hybrid coating comprising 1.0 to 10.0 percent by weight of the hydrophobized cosmetic powder,
dissolving the organotitanate coating agent in a volatile solvent to produce a titanate solution of the organotitanate coating agent;
dissolving the functionalized silicone coating agent in a volatile solvent to produce a solution of the functionalized silicone coating agent;
mixing the solution of the functionalized silicone coating agent with the cosmetic powder or spraying the silicone solution onto the cosmetic powder;
mixing the titanate solution with or spraying the titanate solution onto the cosmetic powder, after mixing the silicone solution with the cosmetic powder or spraying the silicone solution onto the cosmetic powder, to produce a silicone and organotitanate treated cosmetic powder; and
heating the silicone and organotitanate treated cosmetic powder at an elevated temperature, in a range from 60° C. to about 130° C., allowing the silicone and organotitanate treated cosmetic powder to dry resulting in substantial removal of the solvent,
whereby the organotitanate coating agent and the functionalized silicone coating agent form a hybrid coating which is covalently bonded to the cosmetic powder.
28. A coating process for making a hydrophobic coated cosmetic powder, wherein the coating process comprises:
selecting a cosmetic powder, substantially consisting of material selected from the group consisting of titanium dioxide, red iron oxide, yellow iron oxide, black iron oxide, barium lake, mica and silica, with a mean particle size of 0.01 to 20.0 μm to be hydrophobized with a hybrid coating comprising an organotitanate coating agent and a functionalized silicone coating agent;
forming a mixture of the cosmetic powder by combining the cosmetic powder with a liquid medium;
dissolving the organotitanate coating agent in a volatile solvent to produce a titanate solution of the organotitanate coating agent;
dissolving the functionalized silicone coating agent in a volatile solvent to produce a solution of the functionalized silicone coating agent;
applying the solution of organotitanate coating agent to the cosmetic powder in the mixture under mixing or agitation or the equivalent;
applying the solution of functionalized silicone coating to the cosmetic powder in the mixture under mixing or agitation or the equivalent to create a mixture of the silicone and organotitanate treated cosmetic powder;
removing the solvent from the mixture of the silicone and organotitanate treated cosmetic powder to create a silicone and organotitanate treated cosmetic powder; and
heating the silicone and organotitanate treated cosmetic powder at an elevated temperature, in a range from 60° C. to about 130° C., allowing the silicone and organotitanate treated cosmetic powder to dry resulting in substantial removal of the solvent,
whereby the organotitanate coating agent and the functionalized silicone coating agent form a hybrid coating which is covalently bonded to the cosmetic powder, and wherein said hybrid coating is applied to result in the coating comprising 1.0 to 10.0 percent by weight of the hydrophobized cosmetic powder.
29. A coating process as in claim 28 , wherein the organotitanate coating agent and the functionalized silicone coating agent are both dissolved in the same solvent to form the solutions of the coating agents.
30. The process of claim 29 wherein the organio-titanate coating agent is dissolved in volatile solvent(s) and mixed with or sprayed onto the cosmetic powder before the functionalized silicone is mixed with or sprayed on the cosmetic powder.
31. The process of claim 29 wherein the functionalized silicone is dissolved in volatile solvent(s) and mixed with or sprayed onto the cosmetic powder before the organo-titanate coating agent is mixed with or sprayed on the cosmetic powder.