Dental implant incorporating an apatite
A dental implant comprises a composition which comprises a polymeric material which is preferably polyetheretherketone, and an apatite, for example a hydroxy-containing apatite. A prosthodontics device may comprise a dental implant made from polyetheretherketone, an abutment, also made from PEEK, and a crown, which is also made from PEEK by machining from a PEEK disc.
1. A method of making a dental implant, the method comprising:
(i) selecting a composition which comprises a polymeric material and an apatite, wherein said polymeric material comprises a polymeric material which comprises a repeat unit of formula (I)
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2;
wherein the ratio of the wt % of said polymeric material divided by the wt % of said apatite is in the range 1 to 9;
(ii) forming said composition into a shape which defines said dental implant; and
(iii) subjecting the implant to a humid atmosphere which comprises greater than 20% humidity for at least five days and a temperature in the range of 15° C. to 100° C. for at least five days.
2. A method according to claim 1 , wherein the dental implant is configured to cooperate with a superstructure such that the superstructure is releasably securable to the dental implant.
3. A method according to claim 1 wherein the polymeric material has a repeat unit of formula I, wherein t1=1, v1=0 and w1=0.
4. A method according to claim 1 , wherein the polymeric material has a melt viscosity (MV) of at least 0.09 kNsm −2 to 0.5 kNsm −2 .
5. A method according to claim 1 , wherein the level of crystallinity of the polymeric material, measured by DSC, is greater than 25%.
6. A method according to claim 1 , wherein the ratio of the wt % of the polymeric material divided by the wt % of the apatite is in the range 2.3 to 9.
7. A method according to claim 1 , wherein the ratio of the wt % of the polymeric material divided by the wt % of the apatite is in the range 3.8 to 4.2.
8. A method according to claim 1 , wherein the composition includes at least 65 wt % of the polymeric material and includes at least 10 wt % of the apatite; and the sum of the wt % of the polymeric material and the apatite is in the range 90 to 100 wt %.
9. A method according to claim 1 , wherein the apatite is a hydroxyapatite.
10. A method according to claim 1 , wherein said apatite is a hydroxyapatite which consists essentially of calcium, phosphorous, oxygen and hydrogen moieties.
11. A method according to claim 1 , wherein the D50 of said apatite, assessed using laser diffraction and based on a volume distribution, is less than 200 μm.
12. A method according to claim 1 , wherein the D50 of said apatite, assessed using laser diffraction and based on a volume distribution, is less than 20 μm.
13. A method according to claim 1 , wherein the dental implant is arranged to cooperate with a superstructure, wherein said implant includes a female or male element which is arranged to cooperate with a male or female element associated with said superstructure.