Electrolyte film for fuel cell
(Problem) To provide an electrolyte film for fuel cells, capable of achieving both low resistance (film thinning) and high dimensional stability. (Solution) An electrolyte film for fuel cells, the electrolyte film comprising a polymeric electrolyte and a polytetrafluoroethylene (PTFE) porous film, characterized in that a material having an elastic modulus higher than that of the material constituting the PTFE porous film is composited on the inside surfaces of pores of the PTFE porous film, and the composited PTFE porous film has an elastic modulus of at least 150 MPa.
1. An electrolyte membrane for a fuel cell, comprising a polymer electrolyte and a polytetrafluoroethylene (PTFE) porous membrane, wherein:
the inner pore surface of said PTFE porous membrane is compounded with a material higher in the modulus of elasticity than a material constituting said PTFE porous membrane,
wherein said compounded PTFE porous membrane has a modulus of elasticity of 150 MPa or more in at least one direction (MD or TD) or in both directions (MD and TD),
wherein said compounded PTFE porous membrane has a continuous porous structure, and
wherein pores of the continuous porous structure have an average pore diameter between 0.01 and 50 micrometers.
2. The electrolyte membrane according to claim 1 , wherein said polymer electrolyte is a fluorinated ionomer.
3. The electrolyte membrane according to claim 1 , wherein PTFE constituting said PTFE porous membrane is expanded porous PTFE.
4. The electrolyte membrane according to claim 1 , wherein said material having a high modulus of elasticity contains at least one of SiO x , P 2 O 5 , PbO, SrO, BaO and ZrO 2 .
5. The electrolyte membrane according to claim 1 , wherein said material having a high modulus of elasticity contains polybenzimidazole (PBI).
6. The electrolyte membrane according to claim 1 , wherein the content of said material having a high modulus of elasticity is from 1.0 to 11 wt % based on said PTFE porous membrane.
7. The electrolyte membrane according to claim 1 , which further contains a catalyst having a radical-decomposing function.
8. The electrolyte membrane according to claim 7 , wherein said catalyst having a radical-decomposing function contains at least one of cerium, tungsten, ruthenium, palladium, silver, rhodium, zirconium, yttrium, manganese, molybdenum, lead, vanadium and titanium.
9. The electrolyte membrane according to claim 1 , wherein the polytetrafluoroethylene (PTFE) porous membrane has a thickness between 1 and 30 micrometers.
10. The electrolyte membrane according to claim 1 , wherein the polytetrafluoroethylene (PTFE) porous membrane has a porosity of at least 35%.
11. The electrolyte membrane according to claim 1 , wherein the PTFE porous membrane is free of vinylidene fluoride.
12. The electrolyte membrane according to claim 1 , wherein the material having a high modulus of elasticity has a content percentage between 1.0 and 11 weight % based on the polytetrafluoroethylene (PTFE) porous membrane.