Scintillator, scintillator array, radiation detector, and radiation examination device

1. A scintillator, comprising:

a sintered body being 1 mm 3 or less in volume and containing at least one rare earth oxysulfide selected from the group consisting of a gadolinium oxysulfide, an yttrium oxysulfide, and a rutetium oxysulfide;

wherein, in a composition image obtained by observing a cross-section of the sintered body under a scanning electron microscope, the sum of the number of oxide regions that contain at least one of a rare earth oxide different from the rare earth oxysulfide and an impurity metal oxide and the number of sulfide regions that contain at least one of a rare earth sulfide different from the rare earth oxysulfide and an impurity metal sulfide, which exist in a unit area of 500 μm×500 μm, is one or more and five or less,

wherein each of the oxide regions and the sulfide regions has a major axis of 100 μm or less,

wherein, in the composition image, the oxide region and the sulfide region are deeper and darker in color than a rare earth oxysulfide region containing the rare earth oxysulfide,

wherein the rare earth oxide and the rare earth sulfide contain at least one element in common with rare earth elements contained in the rare earth oxysulfide,

wherein the impurity metal oxide and the impurity metal sulfide contain at least one element selected from the group consisting of an alkali metal element, an alkaline earth metal element, and iron,

wherein the sintered body has a plurality of rare earth oxysulfide crystal grains, and

wherein at least some of the oxide regions and the sulfide regions exist at a grain boundary between the grains.

2. The scintillator according to claim 1 , wherein the sintered body is 0.72 mm 3 or less in volume.

3. The scintillator according to claim 1 , wherein a composition of the gadolinium oxysulfide is expressed by

General formula: (Gd 1-a-b Pr a M b ) 2 O 2 S  (1),

where M is at least one element selected from the group consisting of Ce, Yb, Eu, and Tb, a is a number satisfying 0.0001≤a≤0.01, and b is a number satisfying 0≤b<0.005.

4. The scintillator according to claim 1 , wherein an average crystal grain diameter of the grains is 5 μm or more and 30 μm or less.

5. The scintillator according to claim 1 , wherein a maximum diameter of the grains is 50 μm or less.

6. A scintillator array, comprising:

a plurality of scintillators including the scintillator according to claim 1 ; and

a reflection layer provided between a plurality of the scintillators.

7. A radiation detector, comprising:

the scintillator array according to claim 6 , having an X-ray incident surface; and

a photoelectric conversion element provided on a surface opposite to the X-ray incident surface of the scintillator array.

8. The radiation detector according to claim 7 , further comprising:

a surface reflection layer provided on at least one surface of the X-ray incident surface and the surface opposite thereto.

9. A radiation examination device comprising the radiation detector according to claim 7 .

10. A method of manufacturing the scintillator according to claim 1 , comprising the steps of:

washing a rare earth oxysulfide powder with water, the powder having an average particle diameter of 10 μm or less;

heating the powder at a temperature of 700 to 1350° C. for 0.5 to 30 hours in an inert gas atmosphere containing oxygen and sulfur;

molding the powder to form a molded body;

sintering the molded body in a Ta capsule at a temperature of 1400 to 1600° C. and at a pressure of 120 MPa or more for 2 to 7 hours, by a hot isostatic pressing method to form a sintered body; and

heating the sintered body at a temperature of 700 to 1350° C. for 2 to 20 hours in an inert gas atmosphere containing oxygen and sulfur.