Alcohol-removable nail gel and its manufacturing method
An alcohol-removable nail gel comprising the following components in percent by weight: isobornyl acrylate 10-15% hydroxyethyl methacrylate 15-25% trimethylolpropane triacrylate 5-15% (2,4,6-trimethylbenzoyl)diphenylphosphine oxide 5-15% aliphatic urethane acrylate 20-30% cellulose acetate butyrate 15-20% pigments 1-15%. The alcohol removable gel polish, similar in application and function as common one-step gel polish, can be removed with alcohol solution which does not contain acetone, ethyl acetate, butyl acetate or other toxic solvents. Using alcohol-soaked cotton to wrap nails for 10-15 min, the process is environmentally friendly, safe, healthy and not detrimental to human body.
1. An alcohol-removable nail gel comprising the following components in percent by weight:
isobornyl acrylate 10-15%
hydroxyethyl methacrylate 15-25%
trimethylolpropane triacrylate 5-15%
(2,4,6-trimethylbenzoyl)diphenylphosphine oxide 5-15%
aliphatic urethane acrylate 20-30%
cellulose acetate butyrate 15-20%
pigment 1-15%.
2. The alcohol-removable nail gel of claim 1 comprising the following in percent by weight:
isoborneyl acrylate 12%
hydroxyethyl methacrylate 18%
trimethylolpropane triacrylate 10%
(2,4,6-trimethylbenzoyl)diphenylphosphine oxide 7%
aliphatic urethane acrylate 24%
cellulose acetate butyrate 18%
pigment 11%.
3. The alcohol-removable nail gel of claim 1 being a three-in-one nail gel, in which base coat, color lacquer, and top coat are combined for a one-step application.
4. The alcohol-removable nail gel of claim 1 wherein the pigment is selected from the group consisting of CI15850, CI15985, CI17200, CI77492, CI77510, CI77742, CI77491, CI77499, CI77891, and combinations thereof.
5. A method of making the alcohol-removable nail gel of claim 1 comprising the following steps:
(1) mixing isobornyl acrylate, hydroxyethyl methacrylate, trimethylolpropane triacrylate, (2,4,6-trimethyl) benzoyl) diphenylphosphine oxide to form a first mixture, and stirring the first mixture;
(2) adding aliphatic urethane acrylate and cellulose acetate butyrate into the first mixture of step (1) to form a second mixture and stirring the second mixture;
(3) adding the pigment to form a third mixture and stirring the third mixture to make the alcohol removable gel.
6. The method of claim 5 wherein in step (1), the stirring step is carried at a speed of 500-700 r/min for 20-40 minutes.
7. The method of claim 5 wherein in step (2), the stirring is carried out at a speed of 700-900 r/min for 90-120 minutes.
8. The method of claim 5 wherein in step (3), the stirring is carried out at a speed of 400-500 r/min for 5-120 minutes.