Method of forming a coating or of three-dimensional structural elements on substrate surfaces, which is/are formed by TiAl, by laser build-up welding
The invention relates to a method of forming a coating or of three-dimensional structural elements on substrate surfaces which is/are formed by TiAl. Said coating/Said three-dimensional structural elements is/are manufactured by laser build-up welding. The procedure is followed in the method in accordance with the invention that titanium and aluminum are supplied into the region of influence of at least one laser beam in wire and/or band form in a pure or alloyed form in each case as a single wire or a single band. They are melted by the thermal input and in this respect the materials are mixed with one another. The coating or three-dimensional structural elements are thereby formed with TiAl on the substrate surface.
1. A method of forming a coating or three-dimensional structural elements of an ahoy of TiAl on substrate surfaces, comprising,
supplying at least one laser beam at an angle with respect to the substrate surfaces, for laser build-up welding,
supplying at least two individual wires or bands into a region of influence of said at least one laser beam, said at least one laser beam providing thermal input into the region of influence, at least one of said at least two individual wires or bands being of titanium, in pure or alloyed form but without aluminum, at least a second of said at least two individual wires or bands being of aluminum, in pure or alloyed form but without titanium, melting said at least two individual wires or bands by the thermal input of said at least one laser beam, with the melted at least two individual wires or bands mixed with one another and then applied to the substrate surfaces to form said coating or three-dimensional structural elements of said alloy of TiAl on the substrate surfaces.
2. The method in accordance with claim 1 , wherein the coating or three-dimensional structural elements are formed with at least one further metal as an alloy component which is selected from Nb, Ta, Mo, B, Cr and V and C.
3. The method in accordance with claim 1 , wherein each of said at least two individual wires has a wire diameter, each of said bands defines a band cross-section, and said at least two individual wires or bands are supplied into said region of influence at a feed speed, wherein composition of the coating or three-dimensional structural elements are influenced by the wire diameter, the cross-section of one or more bands or the feed speed of the supplied of the at least two individual wires or bands.
4. The method in accordance with claim 1 , wherein the said at least two individual titanium and aluminum wires or bands are supplied by means of a powder filling wire or a powder filling band.
5. The method in accordance with claim 1 , wherein aluminum having a portion in the range 35% to 55% is used in the aluminum wire or band.
6. The method in accordance with claim 1 , wherein the coating or three-dimensional structural elements are formed with γ TiAl phase.
7. The method in accordance with claim 1 , wherein said at least two individual wires or bands are mutually connected.
8. The method in accordance with claim 1 , wherein mutually twisted wires are supplied.
9. The method in accordance with claim 3 , wherein the supply speed of the at least two individual wires or bands are regulated or controlled.