Process for preparing hydrophobically modified alkylene oxide urethane polymer
The present invention relates to a composition comprising an aqueous solution of a hydrophobically modified alkylene oxide urethane polymer (HEUR), a bismuth salt, and at least one sediment abating compound selected from the group consisting of citric acid or a salt thereof, gluconic acid or a salt thereof, and a salt of ethylenediamine tetraacetic acid. The composition with the specific sediment abating compounds shows excellent abatement in sediment and color formation in heat age testing of the solution.
1. A color formation abatement and sediment abatement method comprising the steps of contacting a hydrophobically modified alkylene oxide urethane polymer with water and at least one sediment abating compound, which is citric acid or a salt thereof, gluconic acid or a salt thereof, or a salt of ethylenediamine tetraacetic acid, to form a solution, wherein the hydrophobically modified alkylene oxide urethane polymer comprises from 5 to 1000 ppm of a bismuth salt, wherein the concentration of the sediment abating compound is from 0.05 to 4 weight percent, based on the weight of the solution, and the concentration of the hydrophobically modified alkylene oxide urethane polymer is from 12 to 50 weight percent, based on the weight of the solution.
2. The method of claim 1 wherein the concentration of the hydrophobically modified alkylene oxide urethane polymer is from 15 to 40 weight percent, based on the weight of the solution; and the concentration of the bismuth salt is from 10 to 200 ppm, based on the weight of the solution.
3. The method of claim 2 wherein the concentration of the sediment abating compound is from 0.1 to 3 weight percent, based on the weight of the solution, the pH of the solution is in the range of 2.5 to 6, and the sediment abating compound is citric acid or a salt thereof or a combination thereof.
4. The method of claim 3 , wherein the concentration of the citric acid is in the range of from 0.1 to 1 weight percent, based on the weight of the solution; and wherein the hydrophobically modified alkylene oxide urethane polymer comprises from 10 to 100 ppm of the bismuth salt.
5. A composition comprising an aqueous solution of a hydrophobically modified alkylene oxide urethane polymer, a bismuth salt, and at least one sediment abating compound which is citric acid or a salt thereof, gluconic acid or a salt thereof, or a salt of ethylenediamine tetraacetic acid, wherein the concentration of the hydrophobically modified alkylene oxide urethane polymer is from 12 to 50 weight percent, the concentration of the bismuth salt is from 5 to 1000 ppm, and the concentration of the sediment abating compound is from 0.05 to 4 weight percent, all based on the weight of the solution, wherein the aqueous solution has abated sediment and abated color formation.
6. The composition of claim 5 wherein the concentration of the hydrophobically modified alkylene oxide urethane polymer is from 15 to 40 weight percent, based on the weight of the solution; and the concentration of the bismuth salt is from 10 to 200 ppm, based on the weight of the solution.
7. The composition of claim 6 wherein the concentration of the sediment abating compound is from 0.1 to 3 weight percent, based on the weight of the solution, the pH of the solution is in the range of 2.5 to 6, and the sediment abating compound is citric acid or a salt thereof or a combination thereof.
8. The composition of claim 7 , wherein the concentration of the citric acid is in the range of from 0.1 to 1 weight percent, based on the weight of the solution; and wherein the concentration of the bismuth salt is in the range of 10 to 100 ppm.