Method for fabrication of a hybrid dual phase filler for elastomers
The method for fabricating a hybrid dual phase filler for elastomers includes: impregnation of carbon black with ethanol suspension of magnetite in a ball mill; drying of the dual phase mixture till constant weight; grinding of the dried product in a ball mill; thermal activation under vacuum in a specifically designed reactor followed by a grinding of the final product in a ball mill. The hybrid dual phase filler includes carbon black impregnated with ethanol suspension of magnetite, contains 5 to 50 mass % of magnetite and 95 to 50 mass % of carbon black. Magnetite is a powder and includes up to 5% of SiO 2 , particle size up to 50μ and density of 4.8-5.2 g/cm 3 with a specific surface area (BET/) 400-900 m 2 /g; iodine number—370-750 mg/g; oil number 200-450 ml/100 g; total volume pore 0.5-1.5 cm 3 (STP)/g; micropore surface area 50-90 m 2 /g; external specific surface area 400-900 m 2 /g.
1. A method for fabrication of a hybrid dual phase filler for elastomers based on carbon black and magnetite has been elaborated, the filler includes the carbon black impregnated with ethanol suspension of magnetite in a ball mill, then the dual phase mixture is dried till a constant weight, thereafter the dried product is ground in a ball mill, thermally activated in a reactor designed especially for the purpose, at the end the final product is ground again in a ball mill, the method includes the following steps:
first stage—preparing the ethanol suspension by pouring ethyl alcohol over powder magnetite and successive homogenizing for 1 h;
second stage—impregnating carbon black with the suspension obtained at the first stage and successive treatment in a ball mill for 2 h;
third stage—decanting ethyl alcohol and drying of the obtained dual phase filler at 50° C. for 2 h;
fourth stage—drying till constant weight at temperature risen to 150° C.;
fifth stage—grinding the dried product in a ball mill for 2 h;
sixth stage—thermal activation in a reactor designed especially for the purpose at 440° C. under 10 −2 mm Hg vacuum for 2 h; and
seventh stage—grinding of the final product in a ball mill for 2 h.
2. A dual phase filler made according to the method of claim 1 comprising carbon black impregnated with ethanol suspension of magnetite, which contains 5 to 50 mass % of magnetite and 95 to 50 mass % of carbon black.
3. A dual phase filler for elastomers made according to the method of claim 1 wherein magnetite being a powder comprising up to 5% of SiO 2 , particles size up to 50 μ and density of 4.8-5.2 g/cm 3 .
4. A dual phase filler made according to the method of claim 1 having the following properties: specific surface area (BET/) 400-900 m 2 /g; iodine number —370-750 mg/g; oil number 200-450 ml /100g; total pore volume—0,5-1,5 cm 3 (STP)/g; micropore surface area 50-90 m 2 /g; external specific surface area 400-900 m2/g.