Polyolefin microporous film
There is provided a polyolefin microporous film which is excellent in taking-up stability in a production line and a processing line of the polyolefin microporous film, and further in a line for a battery taking-up step, and hardly generates step deviation when a roll thereof has received an impact. The polyolefin microporous film has a compression elastic modulus of 0.1 to 1,000 kPa, and a ratio of a tensile elastic modulus in the longitudinal direction to a tensile elastic modulus in the transverse direction of 1.5 to 7.8.
1. A biaxially stretched polyolefin microporous film, having a compression elastic modulus of 0.1 to 50 kPa, and a ratio of a tensile elastic modulus in a longitudinal direction to a tensile elastic modulus in a transverse direction of 1.5 to 7.8, wherein
a tensile strength at break in the transverse direction of the biaxially stretched polyolefin microporous film is 50 MPa or more and 500 MPa or less,
an average pore diameter of the polyolefin microporous film is 0.06 to 0.09 μm, and wherein an air permeability of the biaxially stretched polyolefin microporous film is in the range of 10 sec/100 cc to 500 sec/100 cc.
2. The biaxially stretched polyolefin microporous film according to claim 1 , wherein the polyolefin microporous film has a friction coefficient in the transverse direction of 0.2 to 0.7.
3. The biaxially stretched polyolefin microporous film according to claim 1 or 2 , wherein the polyolefin microporous film has a compression elastic modulus of 0.1 to 15 kPa.
4. The biaxially stretched polyolefin microporous film according to claim 1 or 2 , wherein the polyolefin microporous film has been subjected to a hydrophilicizing treatment.
5. The biaxially stretched polyolefin microporous film roll, obtained by rolling the biaxially stretched polyolefin microporous film according to claim 1 or 2 .
6. A separator for a nonaqueous electrolyte secondary battery, comprising the biaxially stretched polyolefin microporous film according to claim 1 or 2 .
7. A nonaqueous electrolyte secondary battery, comprising the separator for the nonaqueous electrolyte secondary battery according to claim 6 , a positive electrode, a negative electrode, and the electrolyte.
8. The biaxially stretched polyolefin microporous film according to claim 1 , wherein an air permeability of the polyolefin microporous film is 80 sec/100 cc or more and 300 sec/100 cc or less.
9. A separator for a nonaqueous electrolyte secondary battery, comprising the biaxially stretched polyolefin microporous film according to claim 8 .
10. A nonaqueous electrolyte secondary battery, comprising the separator for the nonaqueous electrolyte secondary battery according to claim 9 , a positive electrode, a negative electrode, and the electrolyte.
11. The biaxially stretched polyolefin microporous film according to claim 1 further having the compression elastic modulus of 1 to 15 kPa.