Sulfur-crosslinkable rubber mixture and motor vehicle tires
A sulfur-crosslinkable rubber mixture includes from 40 to 100 phr of at least one natural and/or synthetic polyisoprene, and 15 phr or more of at least one hydrocarbon resin which is built up to the extent of 50 to 100 wt. % from aliphatic C 5 monomers and to the extent of 0 to 50 wt. % from further monomers, where the hydrocarbon resin according to formula I) has a Q of from 0.015 [° C.·mol/g] to 0.050 [° C.·mol/g]. Formula I) is defined as Q=softening point [° C.]/centrifuge average Mc [g/mol]. In some aspects, the sulfur-crosslinkable rubber mixture includes 15 to 300 phr of the hydrocarbon resin, or even from 36 to 100 phr of the hydrocarbon resin. The further monomer(s) is or are selected from the group of unsaturated compounds, which can be polymerized cationically, which includes aromatics and/or unsaturated terpenes and/or alkenes and/or cycloalkenes.
1. A sulfur-crosslinkable rubber mixture comprising:
from 40 to 100 phr of at least one natural and/or synthetic polyisoprene;
15 phr or more of at least one hydrocarbon resin which is built up to the extent of 50 to 100 wt. % from aliphatic C 5 monomers and to the extent of 0 to 50 wt. % from further monomers, wherein the hydrocarbon resin according to formula I) has a Q of from 0.015 [° C.·mol/g] to 0.050 [° C.·mol/g], wherein formula I) is defined as Q=softening point [° C.]/centrifuge average Mc [g/mol]; and,
70 to 250 phr of at least one silica;
wherein, after vulcanization, the sulfur-crosslinkable rubber mixture has an elongation at break of from 651% to 722% at room temperature, in accordance with DIN 53 504.
2. The sulfur-crosslinkable rubber mixture of claim 1 comprising 15 to 300 phr of the hydrocarbon resin.
3. The sulfur-crosslinkable rubber mixture of claim 1 comprising 36 to 100 phr of the hydrocarbon resin.
4. The sulfur-crosslinkable rubber mixture of claim 1 wherein the further monomer(s) is or are selected from the group of unsaturated compounds, which can be polymerized cationically, comprising aromatics and/or unsaturated terpenes and/or alkenes and/or cycloalkenes.
5. The sulfur-crosslinkable rubber mixture of claim 4 wherein the further monomer(s) is or are selected from the group consisting of alpha-methylstyrene and/or styrene and/or vinyltoluene and/or indene and/or coumarone and/or methylindene and/or methylcoumarone and/or phenol and/or olefins.
6. The sulfur-crosslinkable rubber mixture of claim 1 wherein the hydrocarbon resin has a softening point according to ASTM E 28 (ring and ball) of from 60 to 99° C.
7. The sulfur-crosslinkable rubber mixture of claim 1 wherein the hydrocarbon resin has a molecular weight Mw (weight average) of from 500 to 4,000 g/mol and a centrifuge average Mc of from 2,500 to 10,000 g/mol.
8. The sulfur-crosslinkable rubber mixture of claim 1 comprising 80 to 180 phr of at least one silica.
9. A vehicle pneumatic tire comprising the sulfur-crosslinkable rubber mixture of claim 1 .
10. The vehicle pneumatic tire as claimed in claim 9 , wherein the sulfur-crosslinkable rubber mixture is comprised in a tread of the vehicle pneumatic tire.