Electric wire and method for producing the same, and multi-core cable and method for producing the same
The electric wire according to one aspect of the present invention is an electric wire comprising an insulated electric wire and one or more coating layers covering the insulated electric wire, wherein at least one layer of the one or more coating layers is formed from a resin composition containing a thermoplastic polyurethane elastomer and an allophanate crosslinking agent. The electric wire having such a characteristic feature is excellent in abrasion resistance and heat resistance and can be produced at low costs.
1. An electric wire comprising an insulated electric wire and one or more coating layers covering the insulated electric wire,
wherein at least one layer of the one or more coating layers is formed from a resin composition containing a thermoplastic polyurethane elastomer and an allophanate crosslinking agent,
wherein the resin composition is a mixture of:
an A agent containing the thermoplastic polyurethane elastomer and
a B agent containing the allophanate crosslinking agent and the thermoplastic polyurethane elastomer or a thermoplastic polyester elastomer.
2. The electric wire according to claim 1 , wherein the coating layers are composed of a plurality of layers and an outermost layer thereof is formed from a resin composition containing a thermoplastic polyurethane elastomer and an allophanate crosslinking agent.
3. The electric wire according to claim 1 , wherein the content of the allophanate crosslinking agent to 100 parts by mass of the thermoplastic polyurethane elastomer in the resin composition is 0.4 parts by mass or more and 15 parts by mass or less.
4. The electric wire according to claim 1 , wherein the B agent contains a monomer as an allophanate crosslinking agent having an isocyanate group.
5. The electric wire according to claim 4 , wherein the content of the monomer in the B agent is 15% by mass or more and 65% by mass or less.
6. The electric wire according to claim 1 , wherein the resin composition further contains a flame retardant.
7. The electric wire according to claim 6 , wherein the content of the flame retardant to 100 parts by mass of the thermoplastic polyurethane elastomer in the resin composition is 3 parts by mass or more and 90 parts by mass or less.
8. A multi-core cable comprising a plurality of insulated electric wires and one or more coating layers covering the plurality of insulated electric wires,
wherein at least one layer of the one or more coating layers is formed from a resin composition containing a thermoplastic polyurethane elastomer and an allophanate crosslinking agent,
wherein the resin composition is a mixture of:
an A agent containing the thermoplastic polyurethane elastomer and
a B agent containing the allophanate crosslinking agent and the thermoplastic polyurethane elastomer or a thermoplastic polyester elastomer.
9. The multi-core cable according to claim 8 , wherein the coating layers are composed of a plurality of layers and an outermost layer thereof is formed from a resin composition containing a thermoplastic polyurethane elastomer and an allophanate crosslinking agent.
10. The multi-core cable according to claim 8 , wherein the coating layers are composed of a plurality of layers and an inner layer thereof is formed from a resin composition containing a thermoplastic polyurethane elastomer and an allophanate crosslinking agent.