Electrical tracking resistance compositions, articles formed therefrom, and methods of manufacture thereof
A composition comprises, based on the total weight of the composition, 45 wt % to 75 wt % of a polyetherimide; and 20 wt % to 45 wt % of talc; and 5 wt % to 15 wt % of a fluorinated polymer; wherein the composition has a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85.
1. A composition comprising, based on the total weight of the composition,
45 wt % to 75 wt % of a polyetherimide;
greater than 20 wt % to 45 wt % of talc having a D95 of 2 microns to 6 microns determined by sedigraph analysis using a Micrometritics Sedigraph 5120 particle size analysis system; and
greater than 5 wt % to 15 wt % of polytetrafluoroethylene;
wherein the composition has a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85,
wherein the polyetherimide comprises units of the formula
wherein R is m-phenylene, p-phenylene, or a combination thereof, and T is the group of the formula —O—Z—O—, wherein Z is a divalent group of the formula
Q being isopropylidene.
2. The composition of claim 1 comprising, based on the total weight of the composition,
50 wt % to 70 wt % of the polyetherimide;
25 wt % to 45 wt % of the talc; and
5 wt % to 8 wt % of the polytetrafluoroethylene;
wherein the composition has:
a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85; and
a tracking voltage of greater than or equal to 250 volts according to ASTM D-3638-85.
3. The composition of claim 2 , wherein the composition has:
a tensile strength greater than or equal to 70 MPa determined according to ASTM D638;
a tensile modulus of greater than or equal to 6500 GPa determined according to ASTM method D638, and
a heat deflection temperature of greater than or equal to 200° C. measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.
4. The composition of claim 1 , further comprising an additive selected from a processing aid, a heat stabilizer, a dye, a flame retardant, or a combination comprising at least one of the foregoing.
5. An insulating material comprising the composition of claim 1 .
6. An article selected from a molded article, a thermoformed article, an extruded film, an extruded sheet, one or more layers of a multi-layer article, a substrate for a coated article, and a substrate for a metallized article made from the composition of claim 1 .
7. An article made from the composition of claim 1 , wherein the article is a solar apparatus, an electrical junction box, an electrical connector, an electrical vehicle charger, an outdoor electrical enclosure, a smart meter enclosure, a smart grid power node, a photovoltaic frame or a miniature circuit breaker.
8. A method of manufacture of an article, comprising molding, extruding, or casting the composition of claim 1 to form the article.
9. A method of controlling the tracking of an electrical current of an article of manufacture, the method comprising: providing a composition of claim 1 , and processing the composition to form an article of manufacture.
10. The method of claim 9 , wherein the article is a solar apparatus, an electrical junction box, an electrical connector, an electrical vehicle charger, an outdoor electrical enclosure, a smart meter enclosure, a smart grid power node, a photovoltaic frame or a miniature circuit breaker.
11. A composition comprising, based on the total weight of the composition,
45 wt % to 55 wt % of a polyetherimide sulfone;
35 wt % to 45 wt % of talc having a D95 of 2 microns to 6 microns determined by sedigraph analysis using a Micrometritics Sedigraph 5120 particle size analysis system; and
8 wt % to 15 wt % of polytetrafluoroethylene;
wherein the composition has:
a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85; and
a tracking voltage of greater than or equal to 300 volts according to ASTM D-3638-85,
wherein the polyetherimide sulfone comprises units of the formula
wherein
R is a divalent group of the formula
wherein Q 1 is —SO 2 —, and
T is the group of the formula —O—Z—O—, wherein Z is a divalent group of the formula
Q being isopropylidene.
12. The composition of claim 11 , wherein the composition has:
a tensile strength greater than or equal to 40 MPa determined according to ASTM D638;
a tensile modulus of greater than or equal to 11,000 GPa determined according to ASTM method D638, and
a heat deflection temperature of greater than or equal to 210° C. measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.