Stainless steel alloys, turbocharger turbine housings formed from the stainless steel alloys, and methods for manufacturing the same
Disclosed is an austenitic stainless steel alloy that includes, by weight, about 22% to about 28% chromium, about 3.5% to about 6.5% nickel, about 1% to about 6% manganese, about 0.5% to about 2.5% silicon, about 0.3% to about 0.6% carbon, about 0.2% to about 0.8% nitrogen, and a balance of iron. Molybdenum, niobium, and tungsten are excluded. The alloy is suitable for use in turbocharger turbine housing applications for temperature up to about 980° C.
1. An turbocharger turbine housing comprising:
an austenitic stainless steel alloy, wherein the austenitic stainless steel alloy consists of, by weight:
24% to 26% chromium;
3.5% to 6.5% nickel;
1% to 6% manganese;
0.5% to 2.5% silicon;
0.3% to 0.6% carbon;
0.2% to 0.5% nitrogen;
up to 0.03% phosphorous;
up to 0.03% sulfur; and
a balance of iron and inevitable/unavoidable impurities.
2. The turbocharger turbine housing of claim 1 consisting of by weight 4.0% to 6.0% nickel.
3. The turbocharger turbine housing of claim 2 consisting of by weight 4.5% to 5.5% nickel.
4. The turbocharger turbine housing of claim 3 consisting of by weight 2.0% to 5.0% manganese.
5. The turbocharger turbine housing of claim 4 consisting of by weight 0.2% to 0.3% nitrogen.
6. The turbocharger turbine housing of claim 1 consisting of by weight 1.5% to 5.5% manganese.
7. The turbocharger turbine housing of claim 6 consisting of by weight 2.0% to 5.0% manganese.
8. The turbocharger turbine housing of claim 7 consisting of by weight 0.2% to 0.3% nitrogen.
9. The turbocharger turbine housing of claim 1 consisting of by weight 1.0% to 2.0% silicon.
10. The turbocharger turbine housing of claim 1 consisting of by weight 0.4% to 0.5% carbon.
11. The turbocharger turbine housing of claim 1 consisting of by weight 0.3% to 0.5% nitrogen.
12. A turbocharger comprising the turbocharger turbine housing of claim 1 that operates at a temperature of up to 980° C.
13. The turbocharger turbine housing of claim 1 consisting of by weight 0.2% to 0.3% nitrogen.
14. A method of fabricating a turbocharger turbine housing, the method comprising the step of:
forming the turbocharger turbine housing from an austenitic stainless steel alloy, wherein the austenitic stainless steel alloy consists of, by weight:
24% to 26% chromium;
3.5% to 6.5% nickel;
1% to 6% manganese;
0.5% to 2.5% silicon;
0.3% to 0.6% carbon;
0.2% to 0.5% nitrogen;
up to 0.03% phosphorous;
up to 0.03% sulfur; and
a balance of iron and inevitable/unavoidable impurities.
15. The method of claim 14 , further comprising forming a turbocharger turbine using the turbocharger turbine housing.