Method for electrochemical reduction of carbon dioxide
View Patent ↗A method of electrochemically reducing CO 2 to form at least one alcohol, preferably ethanol. The method includes (a) contacting an electrode system with an aqueous solution comprising at least one electrolyte and CO 2 , wherein the electrode system comprises a working electrode, a counter electrode, and a reference electrode, wherein the working electrode comprises a base electrode and a coating of a composite comprising graphene nanosheets and Cu 2 O nanoparticles disposed on a surface of the base electrode, and (b) applying a negative potential to the working electrode to reduce the CO 2 and form the at least one alcohol.
1. A method of reducing CO 2 to form ethanol, the method comprising:
(a) contacting an electrode system with an aqueous solution comprising at least one electrolyte and CO 2 ,
wherein the electrode system comprises a working electrode, a counter electrode, and a reference electrode,
wherein the working electrode comprises a copper metal base electrode and a coating of a composite comprising graphene nanosheets and Cu 2 O nanoparticles disposed on a surface of the copper metal base electrode, and
(b) applying a negative potential to the working electrode to reduce the CO 2 and form the ethanol,
wherein ethanol is the predominant alcohol product formed from the reduction of the CO 2 .
2. The method of claim 1 , wherein the contacting is performed in a divided electrochemical cell comprising the counter electrode in a first cell compartment and the working electrode in a second cell compartment, wherein the aqueous solution is present in the first and the second cell compartment.
3. The method of claim 1 , wherein the Cu 2 O nanoparticles are disposed on a surface of the graphene nanosheets in the composite.
4. The method of claim 1 , wherein the Cu 2 O nanoparticles have an average particle size of 20-50 nm.
5. The method of claim 4 , wherein a plurality of the Cu 2 O nanoparticles form a cubic cluster with the longest edge of 60-200 nm.
6. The method of claim 5 , wherein the graphene nanosheets enclose the cubic cluster of the Cu 2 O nanoparticles in the composite.
7. The method of claim 1 , wherein the composite has a weight ratio of the graphene nanosheets: the Cu 2 O nanoparticles in the range of 0.2-0.8.
8. The method of claim 1 , wherein an amount of the coating of the composite disposed on the surface of the copper metal base electrode is 0.01-0.5 mg/cm 2 surface area of the copper metal base electrode.
9. The method of claim 1 , wherein the reference electrode is an Ag/AgCl reference electrode, and wherein the negative potential is from −0.9 V to −1.3 V.
10. The method of claim 9 , wherein the CO 2 is reduced to the ethanol at the working electrode with a faradaic efficiency of 5-10%.
11. The method of claim 9 , wherein the working electrode has a current density of 0.5-3 mA/cm 2 .
12. The method of claim 1 , wherein the aqueous solution is saturated with the CO 2 .