Resin composition for automotive cable material and cable using the same
Disclosed are a resin composition for a cable material and a cable used for a vehicle and a method of manufacturing the cable thereof. In particularly, by controlling the components such as a polypropylene content, a flame retardant content and the like in a base resin, and containing a high crystalline homo polypropylene (PP) resin and a high crystalline block polypropylene resin in the base resin in a specific ratio, the resin composition provides excellent physical properties such as abrasion resistance and flexibility resistance and has reduced weight effect when a cable is manufactured using the resin composition.
1. A resin composition comprising:
a mixture of a base resin and a magnesium hydroxide flame retardant;
an antioxidant; and
a lubricant,
wherein the resin composition comprises an amount of about 2 to 5 parts by weight of the antioxidant and an amount of about 0.5 to 2 parts by weight of the lubricant with respect to 100 parts by weight of the mixture,
wherein the mixture comprises an amount of about 40 to 60% by weight of the base resin and an amount of about 60 to 40% by weight of the magnesium hydroxide flame retardant, based on the total weight of the mixture,
wherein a surface of the magnesium hydroxide flame retardant is treated with silane or aliphatic or polymeric fatty acid,
wherein the base resin comprises 100 parts by weight of a high crystalline polypropylene resin, an amount of about 5 to 10 parts by weight of a modified polypropylene and an amount of about 15 to 20 parts by weight of an elastomer,
wherein the high crystalline polypropylene resin comprises an amount of about 60 to 90% by weight of a high crystalline homo polypropylene resin and an amount of about 10 to 40% by weight of a high crystalline block polypropylene resin, based on the total weight of the high crystalline polypropylene resin, and
wherein the base resin further comprises maleic acid in an amount of about 0.1 to 3 parts by weight with respect to 100 parts by weight of the base resin; and an initiator.
2. The resin composition of claim 1 , wherein the high crystalline polypropylene resin has a hardness (R Scale) of about 100 or greater, a melting index (MI) of about 5 to 50 g/10 min, and a degree of crystallization of about 50% or greater.
3. The resin composition of claim 1 consisting essentially of:
an amount of 100 parts by weight of the mixture that comprises the base resin and the magnesium hydroxide flame retardant;
an amount of about 2 to 5 parts by weight of the antioxidant; and
an amount of about 0.5 to 2 parts by weight of the lubricant,
wherein the mixture comprises an amount of about 40 to 60% by weight of the base resin and an amount of about 60 to 40% by weight of the magnesium hydroxide flame retardant, based on the total weight of the mixture in the resin composition.
4. A method for preparing a cable material for a vehicle comprising,
extruding a resin composition,
wherein the resin composition comprises:
a mixture of a base resin and a magnesium hydroxide flame retardant;
an antioxidant; and
a lubricant,
wherein the resin composition comprises an amount of about 2 to 5 parts by weight of the antioxidant and an amount of about 0.5 to 2 parts by weight of the lubricant with respect to 100 parts by weight of the mixture,
wherein the mixture comprises an amount of about 40 to 60% by weight of the base resin and an amount of about 60 to 40% by weight of the magnesium hydroxide flame retardant based on the total weight of the mixture;
wherein a surface of the magnesium hydroxide flame retardant is treated with silane or aliphatic or polymeric fatty acid,
wherein the base resin comprises 100 parts by weight of a high crystalline polypropylene resin, an amount of about 5 to 10 parts by weight of a modified polypropylene, and an amount of about 15 to 20 parts by weight of an elastomer,
wherein the high crystalline polypropylene resin comprises an amount of about 60 to 90% by weight of a high crystalline homo polypropylene resin and an amount of about 10 to 40% by weight of a high crystalline block polypropylene resin, based on the total weight of the high crystalline polypropylene resin, and
wherein the base resin further comprises maleic acid in an amount of about 0.1 to 3 parts by weight with respect to 100 parts by weight of the base resin; and an initiator, and
wherein the extrusion was carried out at a temperature of about 180 to 230° C.
5. A cable comprising:
a cable cover comprising a resin composition of claim 1 , and
a conductor comprising copper alloy or copper clad steel (CCS).
6. The cable of claim 5 , wherein the copper alloy or CCS has a strength of 700 MPa or greater.
7. The cable of claim 5 , wherein the copper alloy is an alloy conductor containing an amount of about 0.10 to 0.45% of Sn based on the total weigh of the copper alloy, and
wherein the copper alloy has a strength of about 700 to 900 MPa and conductivity of about 70 to 90% according to International Annealed Copper Standard (IACS).
8. The cable of claim 5 , wherein the CCS is a copper covered conductor having a copper area of about 30 to 40%, a conductivity of about 35 to 45% IACS, and, as for elongation, a strength property of about 700 to 900 MPa when softened by about 1 to 10%.
9. A vehicle comprising a cable of claim 5 .