Method of selective laser brazing
A method of selective laser brazing is provided. The method includes providing a powder including a plurality of parent core particles and a plurality of braze particles, setting a temperature of an energy source, applying the energy source to the powder, and allowing the heated powder to solidify. The plurality of parent core particles are fused together by the plurality of braze material into a desired component.
1. A method of selective laser brazing, comprising:
preparing a powder including a plurality of parent core particles and a plurality of braze particles;
setting a temperature of an energy source to a temperature above the melting point (liquidus) of the braze particles and below solidus of the parent core particles;
applying the energy source to the powder at the set temperature so that the braze particles melt and distribute by capillary action between the parent core particles while the parent core particles do not melt; and
allowing the heated powder to solidify,
wherein the plurality of parent core particles are fused together by the solidified distribution of the plurality of braze material into a desired solid component.
2. The method as claimed in claim 1 , wherein the preparing includes coating each of the plurality of parent core particles with a braze material.
3. The method as claimed in claim 1 , wherein the preparing includes mixing the plurality of parent core particles with the plurality of braze particles.
4. The method as claimed in claim 1 , wherein the preparing includes disposing braze particles against each parent core particle such that a plurality of conglomerate particles are formed.
5. The method as claimed in claim 1 , wherein the plurality of parent core particles each include a diameter between 10 and 60 μm.
6. The method as claimed in claim 1 , wherein the parent core particles includes a melting point that is above 2000° C.
7. The method as claimed in claim 1 , wherein the applying includes scanning, with the energy source, a plurality of layers generated from a three-dimensional description of the component on the surface of a powder bed.
8. The method as claimed in claim 1 , wherein the applying includes focusing the energy source onto the powder which has been fed onto a substrate in order to create a deposit of material.
9. The method as claimed in claim 1 , wherein the plurality of braze particles comprise nickel and the plurality of parent core particles comprise yttria stabilized zirconia.
10. The method as claimed in claim 1 , wherein the plurality of braze particles comprise a braze alloy including a melting point suppressant material.
11. The method as claimed in claim 10 , wherein the melting point suppressant material is selected from the group consisting of boron, phosphorous, and silicon.
12. The method as claimed in claim 11 , wherein after the allowing, the method includes subjecting the component to a post process heat treatment to diffuse the melting point suppressant material.
13. The method as claimed in claim 1 , wherein the plurality of braze particles comprise a braze alloy including a wetting agent material.
14. The method as claimed in claim 13 , wherein the wetting agent material is selected from the group consisting of zirconium and silicon.
15. The method as claimed in claim 1 , wherein the energy source is a laser beam.
16. The method as claimed in claim 1 , wherein the energy source is a plasma arc beam.
17. The method as claimed in claim 1 , wherein the energy source is an electron beam.