Multilayer, microporous polyolefin membrane, and production method thereof

1. A multilayer, microporous polyolefin membrane, comprising:

a first surface layer comprising a first microporous layer containing polypropylene, wherein a polypropylene distribution in the first microporous layer is substantially uniform along an in-plane direction,

wherein an electrolyte injection performance of the multilayer, microporous polyolefin membrane is 20 seconds or less, and wherein air permeability normalized for the membrane thickness of the membrane of 20 μm is 20 sec/100 cm 3 /20 μm or greater, and wherein air permeability of the membrane is 285 sec/100 cm 3 or less,

wherein a pin puncture strength (Punc 1 ) of the first microporous layer is between 4500 mN/20 μm and 7000 mN/20 μm, and a porosity (Po 1 ) of the first microporous layer is between 40% and 50%,

wherein the pin puncture strength (Punc 1 ) of the first microporous layer and the porosity (Po 1 ) of the first microporous layer satisfy a relationship described in Formula (A) below:

110≤ Po 1 +0.01275×Punc 1 ≤122  Formula (A), and

wherein, Po 1 is the porosity (%) of the first microporous layer, and Punc 1 is the pin puncture strength (mN/20 μm) normalized for the membrane thickness of the first microporous layer of 20 μm.

2. The multilayer, microporous polyolefin membrane according to claim 1 , wherein the first surface layer further comprises polyethylene, and wherein a normalized polypropylene/polyethylene ratio in the first microporous layer determined by Raman spectroscopy has an average value of 0.5 or greater, a standard deviation of 0.2 or less, and kurtosis between −1.0 and 1.0.

3. The multilayer, microporous polyolefin membrane according to claim 1 , wherein the polypropylene has an average molecular weight greater than 6.0×10 4 and less than 3.0×10 5 , and wherein the first microporous layer contains at least 0.5% polypropylene by weight and contains less than 5.0% polypropylene by weight.

4. The multilayer, microporous polyolefin membrane according to claim 1 , wherein the first microporous layer comprises a first polyolefin resin, and the first polyolefin resin comprises:

polyethylene having an average molecular weight of less than 1.0×10 6 ,

ultra high molecular weight polyethylene having an average molecular weight of 1.0×10 6 or greater, and

polypropylene having an average molecular weight of greater than 6.0×10 4 and less than 3.0×10 5 .

5. The multilayer, microporous polyolefin membrane according to claim 4 , wherein the first polyolefin resin comprises:

high density polyethylene having an average molecular weight of 5.0×10 4 or greater and less than 5.0×10 5 , and a concentration between 45.0% by weight and 98.5% by weight,

ultra high molecular weight polyethylene having an average molecular weight of at least 1.0×10 6 and less than 3.0×10 6 , and a concentration between 1.0% by weight and 55.0% by weight, and

polypropylene having an average molecular weight of greater than 6.0×10 4 and less than 3.0×10 5 , and a concentration of at least 0.5% by weight and less than 5.0% by weight.

6. The multilayer, microporous polyolefin membrane according to claim 1 , comprising a second microporous layer formed from a second polyolefin resin, wherein the second microporous layer is arranged in between the first surface layer and a surface layer.

7. A multilayer, microporous polyolefin membrane, comprising:

a first surface layer comprising a first microporous layer containing polypropylene, wherein a polypropylene distribution in the first microporous layer is substantially uniform along a first in-plane direction,

wherein an electrolyte injection performance of the multilayer, microporous polyolefin membrane is 20 seconds or less, and wherein air permeability normalized for the membrane thickness of the membrane of 20 μm is 20 sec/100 cm 3 /20 μm or greater, and wherein air permeability of the membrane is 285 sec/100 cm 3 or less; and

a second microporous layer formed from a second polyolefin resin,

wherein the multilayer, microporous polyolefin membrane has a three-layer structure in which the second microporous layer is arranged in between the first surface layer and a second surface layer, wherein the second surface layer comprises a third microporous layer containing polypropylene, wherein a polypropylene distribution in the third microporous layer is substantially uniform along a second in-plane direction.

8. The multilayer, microporous polyolefin membrane according to claim 7 , wherein the first surface layer further comprises polyethylene, and wherein a normalized polypropylene/polyethylene ratio in the first microporous layer determined by Raman spectroscopy has an average value of 0.5 or greater, a standard deviation of 0.2 or less, and kurtosis between −1.0 and 1.0.

9. The multilayer, microporous polyolefin membrane according to claim 7 , wherein the polypropylene has an average molecular weight greater than 6.0×10 4 and less than 3.0×10 5 , and wherein the first microporous layer contains at least 0.5% polypropylene by weight and contains less than 5.0% polypropylene by weight.

10. The multilayer, microporous polyolefin membrane according to claim 7 , wherein a pin puncture strength (Punc 1 ) of the first microporous layer is between 4500 mN/20 μm and 7000 mN/20 μm, and a porosity (Po 1 ) of the first microporous layer is between 40% and 50%.

11. The multilayer, microporous polyolefin membrane according to claim 10 , wherein the pin puncture strength (Punc 1 ) of the first microporous layer and the porosity (Po 1 ) of the first microporous layer satisfy a relationship described in Formula (A) below:

110≤ Po 1 +0.01275×Punc 1 ≤122  Formula (A),

wherein, Po 1 is the porosity (%) of the first microporous layer, and Punc 1 is the pin puncture strength (mN/20 μm) normalized for the membrane thickness of the first microporous layer of 20 μm.

12. The multilayer, microporous polyolefin membrane according to claim 7 , wherein the first microporous layer comprises a first polyolefin resin, and the first polyolefin resin comprises:

polyethylene having an average molecular weight of less than 1.0×10 6 ,

ultra high molecular weight polyethylene having an average molecular weight of 1.0×10 6 or greater, and

polypropylene having an average molecular weight of greater than 6.0×10 4 and less than 3.0×10 5 .

13. The multilayer, microporous polyolefin membrane according to claim 12 , wherein the first polyolefin resin comprises:

high density polyethylene having an average molecular weight of 5.0×10 4 or greater and less than 5.0×10 5 , and a concentration between 45.0% by weight and 98.5% by weight,

ultra high molecular weight polyethylene having an average molecular weight of at least 1.0×10 6 and less than 3.0×10 6 , and a concentration between 1.0% by weight and 55.0% by weight, and

polypropylene having an average molecular weight of greater than 6.0×10 4 and less than 3.0×10 5 , and a concentration of at least 0.5% by weight and less than 5.0% by weight.

14. The multilayer, microporous polyolefin membrane according to claim 7 , wherein the second polyolefin resin comprises:

high density polyethylene having an average molecular weight of at least 5.0×10 4 and less than 5.0×10 5 , and a concentration of between 50.0% and 99.0% by weight of the second polyolefin resin, and

ultra high molecular weight polyethylene having an average molecular weight of at least 1.0×10 6 and less than 3.0×10 6 , and a concentration of between 1.0% and 50.0% by weight of the second polyolefin resin, and

wherein the second polyolefin resin does not contain polypropylene.

15. The multilayer, microporous polyolefin membrane according to claim 14 , wherein the second microporous layer is substantially uniform along an in-plane direction.

16. A multilayer, microporous polyolefin membrane, comprising:

a first surface layer comprising a first microporous layer containing polypropylene, wherein a polypropylene distribution in the first microporous layer is substantially uniform along an in-plane direction,

wherein an electrolyte injection performance of the multilayer, microporous polyolefin membrane is 20 seconds or less, and wherein air permeability normalized for the membrane thickness of the membrane of 20 μm is 20 sec/100 cm 3 /20 μm or greater, and wherein air permeability of the membrane is 285 sec/100 cm 3 or less; and

a second microporous layer formed from a second polyolefin resin, wherein the second microporous layer is arranged in between the first surface layer and a surface layer, and wherein the second polyolefin resin comprises:

high density polyethylene having an average molecular weight of at least 5.0×10 4 and less than 5.0×10 5 , and a concentration of between 50.0% and 99.0% by weight of the second polyolefin resin, and

ultra high molecular weight polyethylene having an average molecular weight of at least 1.0×10 6 and less than 3.0×10 6 , and a concentration of between 1.0% and 50.0% by weight of the second polyolefin resin, and

wherein the second polyolefin resin does not contain polypropylene.

17. The multilayer, microporous polyolefin membrane according to claim 16 , wherein the first surface layer further comprises polyethylene, and wherein a normalized polypropylene/polyethylene ratio in the first microporous layer determined by Raman spectroscopy has an average value of 0.5 or greater, a standard deviation of 0.2 or less, and kurtosis between −1.0 and 1.0.

18. The multilayer, microporous polyolefin membrane according to claim 16 , wherein the polypropylene has an average molecular weight greater than 6.0×10 4 and less than 3.0×10 5 , and wherein the first microporous layer contains at least 0.5% polypropylene by weight and contains less than 5.0% polypropylene by weight.

19. The multilayer, microporous polyolefin membrane according to claim 16 , wherein a pin puncture strength (Punc 1 ) of the first microporous layer is between 4500 mN/20 μm and 7000 mN/20 μm, wherein a porosity (Po 1 ) of the first microporous layer is between 40% and 50%, and wherein the pin puncture strength (Punc 1 ) of the first microporous layer and the porosity (Po 1 ) of the first microporous layer satisfy a relationship described in Formula (A) below:

110≤ Po 1 +0.01275×Punc 1 ≤122  Formula (A),

wherein, Po 1 is the porosity (%) of the first microporous layer, and Punc 1 is the pin puncture strength (mN/20 μm) normalized for the membrane thickness of the first microporous layer of 20 μm.

20. The multilayer, microporous polyolefin membrane according to claim 16 , wherein the first microporous layer comprises a first polyolefin resin, and the first polyolefin resin comprises:

polyethylene having an average molecular weight of less than 1.0×10 6 ,

ultra high molecular weight polyethylene having an average molecular weight of 1.0×10 6 or greater, and

polypropylene having an average molecular weight of greater than 6.0×10 4 and less than 3.0×10 5 ,

wherein the first polyolefin resin comprises:

high density polyethylene having an average molecular weight of 5.0×10 4 or greater and less than 5.0×10 5 , and a concentration between 45.0% by weight and 98.5% by weight,

ultra high molecular weight polyethylene having an average molecular weight of at least 1.0×10 6 and less than 3.0×10 6 , and a concentration between 1.0% by weight and 55.0% by weight, and

polypropylene having an average molecular weight of greater than 6.0×10 4 and less than 3.0×10 5 , and a concentration of at least 0.5% by weight and less than 5.0% by weight.

21. The multilayer, microporous polyolefin membrane according to claim 16 , wherein the multilayer, microporous polyolefin membrane has a three-layer structure in which the second microporous layer is arranged in between the first surface layer and a second surface layer, wherein the second surface layer comprises a second microporous layer containing polypropylene, wherein a polypropylene distribution in the second microporous layer is substantially uniform along an in-plane direction.